采用不同工艺对Ti3Al-Nb合金进行了激光熔凝实验.分别运用OM,SEM,XRD和EP对熔化区显微组织进行了观察与分析.结果表明,熔化区由成分偏离平衡成分的β相组成,呈弧形分层特征,有贯穿层间的晶界;晶粒中有特征尺寸为400-750 nm的柱状亚结构和等轴亚结构.基于三维热传导模型,借助Mathematic 4.0计算软件对熔池形状和温度分布进行了数值模拟,计算结果与实验吻合.
参考文献
| [1] | Froes F H, Suryanarayana C, Eliezer D. J Mater Sci, 1992;27:5113 |
| [2] | Bozorg Kashani S F, Fwest D R, Rawings R D. Titanium '95, Vol 2, London: Institute of Materials, 1996:473 |
| [3] | Shinya M, Takemoto M. Corros Eng, 1992; 41:470 |
| [4] | McElroy S, Yang D, Reddy R G. J Mater Eng Perform,2000; 9:506 |
| [5] | Abboud J H, West D R F. J Mater Sci, 1992; 27:4201 |
| [6] | Uenishi K, Sugimoto A, Kobayashi K F. Z Metallkd, 1992;83:241 |
| [7] | Hara M, Kitagawa Y, Sato Y, Kawashima A. J Surf Finish Soc Jpn, 1999; 50:630 |
| [8] | Abboud J H, West D R F. J Mater Sci Lett, 1992; 11:1479 |
| [9] | Hirose A, Ueda T, Kobayashi K F. Mater Sci Eng, 1993;160A: 143 |
| [10] | Nwobu A I P, Rawlings B D, West D R F. Acta Mater,1999; 47:631 |
| [11] | Wen D, Cai Q K, Liu C S, Guo Y J, Zhao Y H. Acta Metall Sin (Eng Lett), 1992; 12:860 |
| [12] | 何秀丽,王华明,郑启光,许德生.金属学报,1998;34:983 |
| [13] | 何秀丽,王华明.中国有色金属学报,2000;10:790 |
| [14] | 于利根,李晓轩,王华明.稀有金属材料与工程,2000;29:328 |
| [15] | 关镇中.激光加工工艺手册.北京:中国计量出版社 |
| [16] | 徐瑞.哈尔滨工业大学博士学位论文,1995 |
| [17] | Malakondaiah G, Nicholas T. Metall Mater Trans, 1994;25A: 183 |
| [18] | Muraleedharan K, Gogia A K, Nandy T K, Banerjee D,Lele S. Metall Trans, 1992; 23A: 400 |
| [19] | Lu B, Yang R, Cui Y Y, Li D. Metall Mater Trans, 2000;31A: 2205 |
| [20] | Cline H E, Anthony T R. J Appl Phys, 1977; 48:3895 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%