研究了热等静压态的NiAl-9Mo合金在850-950℃和50-100 MPa下的蠕变行为.在试验应力和温度下,该合金蠕变曲线呈现出较短的减速阶段和较长的稳态蠕变阶段;其稳态蠕变速率可用幂指数蠕变方程来描述,应力指数值为4.75±0.25,表观激活能为410.5±4.5 kJ/mol.加速蠕变阶段蠕变速率的增加是由于裂纹的形成和扩展,且其断裂数据遵循Monkman-Grant规律蠕变断口呈现出塑性断裂和沿晶蠕变断裂的混合特征,但后者比例较大,同一温度下随着应力的增大,沿晶断裂的比例呈现下降的趋势.
参考文献
| [1] | Johnson D R, Chen X F, Oliver B F, Noebe R D, Whittenberger J D. Intermetallics, 1995; 3:99 |
| [2] | Kumar K S, Mamar S K, Viswanadham S K. Acta Metall Mater, 1992; 40:1201 |
| [3] | Cui C Y, Chen Y X, Guo J T, Li D X, Ye H Q. Mater Lett, 2000; 43:303 |
| [4] | Guo J T, Cui C Y, Chen Y X, Li D X, Ye H Q. Intermetallics, 2001; 9:28 |
| [5] | Whittenberger J D. J Mater Sci, 1987; 22:394 |
| [6] | Whittenberger J D, Reviere R, Noebe R D, Oliver B F.Scr Metall Mater, 1992; 26:987 |
| [7] | Whittenberger J D, Noebe R D, Johnson D R, Oliver B F. Intermetallics, 1997; 5:173 |
| [8] | Whittenberger J D. J Mater Sci, 1988; 22:235 |
| [9] | Qi Y H, Guo J T, Cui C Y, Li G S. Acta Metall Sin, 2001;37:957(齐义辉,郭建亭,崔传勇,李谷松.金属学报,2001;37:957) |
| [10] | Yuan C, Guo J T, Yang H C, Wang S H. Acta Metall Sin,1998; 34:858(袁超,郭建亭,杨洪才,王淑荷.金属学报,1998;34:858) |
| [11] | Dennison J P, Holrnes P D, Wilshire B. Mater Sci Eng,1978; 33:35 |
| [12] | Cui C Y, Guo J T, Qi Y H, Ye H Q. Acta Metall Sin,accepted(崔传勇,郭建亭,齐义辉,叶恒强金属学报,待发表) |
| [13] | Coble R L. J Appl Phys, 1963; 34:1679 |
| [14] | Sherby O D, Burke P M. Prog Mater Sci, 1968; 13:325 |
| [15] | Weetman J. J Appl Phys, 1957; 28:362 |
| [16] | Cannon W R, Sherby O D. Metall Trans, 1970; 1:1030 |
| [17] | Rudy M, Sauthoff G. Mater Sci Eng, 1986; 81:525 |
| [18] | Pugh J W. Trans ASM, 1955; 47:984 |
| [19] | Chen R S. Ph D Thesis, Dalian University of Technolodge,Dalian, 1999(陈荣石.大连理工大学博士论文,大连,1999) |
| [20] | Ren W L, Guo J T, Li G S, Zhou J Y. J Mater Sci Technol,accepted |
| [21] | Monkman F C, Grant N. J Proc ASTM, 1956; 56:593 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%