采用OM,SEM,EDS及XRD法研究了聚焦光束预涂粉末堆焊和送粉堆焊过程的熔池凝固特点.分析了堆焊层微观组织的形成机理.实验结果表明.大线能量光束堆焊层由底部具有外延生长特征的γ(Fe,Ni)平面晶及逆热流择优生长的γ(Fe,Ni)树枝晶组成.而且堆焊层表层树枝晶与光束扫描方向的夹角小于堆焊层底部树枝晶与光束扫描方向的夹角.送粉堆焊及预涂粉末堆焊层中的基底相均为γ(Fe,Ni)相.后析出的γ(Fe,Ni)富Cr.预涂粉末堆焊时堆焊层局部区域Cr,C元素的富集导致了Cr23C6析出.送粉堆焊过程中熔池过热度小.B,Si等造渣元素的烧损少.堆焊层中局部区域富集的B元素优先与Cr元素结合以Cr5B3形式析出.
参考文献
| [1] | Shan J G, Wu A P, Zhang D, Ren J L. Paton Weld J,2000; 9-10:164 |
| [2] | Shan J G, Zhang D, Ren J. Chin J Mech Eng, 2001;37(10): 35(单际国,张迪,任家烈.机械工程学报,2001;37(10):35) |
| [3] | Zhou Z F, Zhang W Y. Welding Metallurg and Metal Weldability. Beijing: Machinery Industry Press, 1992:98(周振丰,张文钺.焊接冶金与金属焊接性.北京:机械工业出版社,1992:98) |
| [4] | Zheng S A, Zhang Y M, Ma Y Q, Huang J L. J Iron Steel Res, 1996; 8(4): 46(郑世安,张一民,马运庆,黄金亮.钢铁研究学报,1996;8(4):46) |
| [5] | Lei T, Ouyang J H, Pei Y T, Zhou Y. Surf Eng, 1996; 12:55 |
| [6] | Hidouci A, Pelleter J M, Ducoin F, Dezert D, Guerjouma R E. Surf Coat Technol, 2000; 123:17 |
| [7] | Li Q, Wang F C, Lei T Q, Chen Y B, Ouyang J H, Yang D Z. Chin J Nonferrous Met, 1998, 8:201(李强.王富耻,雷廷权,陈彦斌,欧阳家虎,杨德.中国有色金属学报,1998;8:201) |
| [8] | Shan J G, Ding J C, Ren J L. Trans Chin Weld Inst, 2001;22(4): 1(单际国,丁建春,任家烈.焊接学报,2001,22(4):1) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%