研究了高密度脉冲电流对A356铝合金低温熔体凝固组织的影响.实验中对680和630℃的低温熔体施加脉冲电流处理,对比试验和凝固曲线测试结果表明.低温熔体中施加脉冲电流有利于增大凝固过冷度.提高冷却速率.缩短凝固时间.细化凝固组织.同时.经脉冲电流处理后.随熔体的保温时间延长.凝固组织逐渐粗化.分析认为.低温熔体结构比凝固过程本身更能影响最终凝固组织.
参考文献
| [1] | Misra A K. Metall Trans, 1985; 16A: 1354 |
| [2] | Ahmed S, McKannan E C. Mater Sci Technol, 1994; 10:941 |
| [3] | Nakada M, Shiohara Y, Flemings M C. ISIJ Int, 1990;30(1): 27 |
| [4] | Li J M, Li S L, Li J. Scr Metall Mater, 1994; 31:1691 |
| [5] | Barnak J, Sprecher A F S, Conrad H. Scr Metall Mater,1995; 32:879 |
| [6] | Zhang L, Bian X F, Ma J J. Foundry, 1995; 10:7(张林,边秀房,马家骥.铸造.1995;10:7) |
| [7] | Li P J, Gui M C, Jia J. Foundry, 1995; 9:15(李培杰.桂满昌,贾均.铸造.1995;9:15) |
| [8] | Wang W M, Bian X F, Qin J Y. Trans Nonferrous Met Soc Chin, 1998; 8:230 |
| [9] | Moon F C. Magneto-solid Mechanics. New York: A Wiley-Interscience Publication, 1984:1 |
| [10] | Nakada M. Master Thesis. Massachusetts Inst Tech, 1985 |
| [11] | Yah H C, He G H, Zhou B L. Acta Metall Sin, 1997; 33:352(鄢红春,何冠虎,周本濂.金属学报,1997;33:352) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%