Fe-Nb-C合金内耗测试表明:700℃,1 h水淬合金的Snoek峰较低,而且含Nb越多,Snoek峰高(hs)越低.与通常铁基材料不同,变形导致Fe-Nb-C合金的hs增强:对于含Nb(≥0.06%,质量分数,下同)较低的合金,"Snoek阻尼温区"(室温-150℃)内耗增强显著,其Snoek峰高温支明显抬起、甚至形成混合双峰;对于含Nb≥0.3%的合金,hs增强甚微,仍是一对称的Snoek峰,并在80-130℃间形成-分立峰.降温SKK峰向低温移动,但峰高(hcsKK)未减低,含Nb较低合金的hcSKK都明显高于hhSKK.
参考文献
| [1] | ЛившицЛС,ПаничиСИ,Е.А.Ассонова ,ФММ 1962;13:576 |
| [2] | Yu N,Wang D J,Ji J W.Acta Met Sin,1999;12:694 |
| [3] | Zeng G Y,Che Y Y,Jin H Z,Ji J W,Huang R Z,Liu J M,Hua Q Z,Zhou X.Acta Metall Sin,1997;33:913(曾桂义,车韵怡,金洪征,戢景文,黄镇如,刘建民,华侨柱,周星.金属学报,1997;33:913) |
| [4] | Ji J W,Lai Z H,Wu Y Q,Zhang G F,Li G Y.Acta Metall Sin,1991;27:408(戢景文,赖祖涵,吴玉琴,张国福,李广义.金属学报,1991;27:408) |
| [5] | Magalas L B.J Physics,1996;4:163 |
| [6] | Ji J W,Wei Q J,Zhang G F,Lai Z H,Chen L G.Acta Metall Sin,1992;28:A207(戢景文,魏全金,张国福,赖祖涵,陈连国.金属学报,1992;28:A207) |
| [7] | Honeycombe R W K.Steels,Microstructure and Properties,Edward Arnold,1981:5 |
| [8] | Silcock J M.JISI,1963;201:409 |
| [9] | Che Y Y,Liu F D,Hua Q Z,Ji J W,Hua J Z,Liu J M,Huang R Z.Acta Metall Sin,1998;34:831(车韵怡,刘芬娣,华桥柱,戢景文,华侨柱,刘建民,黄镇如金属学报,1998;34:31) |
| [10] | Ji J W,Zhao Z Q,He L D,Dian D Q.Acta Phys Sin,1985;34:1620(戢景文,赵增祺,贺礼端,耿殿奇.物理学报,1985;34:1620) |
| [11] | Nowick A S,Berry B S.Anelastic Relaxation in Crystalline in Solids,Academic Press,INC New York and London,1972:403 |
| [12] | Ino H,Segeno T.Acta Metall,1967;15:1197 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%