在热模拟单向压缩实验中,通过形变参数的变化考察了Q235碳素钢应变强化相变的基本规律及铁素体晶粒细化效果结果表明,铁素体的超细化在热力学上是由于应变强化相变最大限度地提高了相变过冷度,在动力学上是由于形核集中在局部的高应变区,同时在转变过程中形变不断产生新的形核地点并抑制铁素体生长的结果实现铁素体的超细化需要一最小应变量及一定的应变速率,以使转变完毕并抑制铁素体的生长及形变成长条状应变明显削弱了奥氏体晶粒尺寸的差异带来的铁素体尺寸的差异.应变造成的铁素体动态再结晶进一步细化了晶粒,这种特征是动态转变所特有的此外,还比较了应变强化相变与无应变及传统控轧控冷过程铁素体形成时的差异.
参考文献
| [1] | Yada H, Matsumura Y, Nakajima K. United States Patent, No.4466842 1984 |
| [2] | Matsumura Y, Yada H. Trans ISIJ, 1987,27:492 |
| [3] | Yang P, Fu Y Y, Cui F E, Sun Z Q. Acta Metall Sin. 2001,37:617(杨平,傅云义,崔凤娥,孙祖庆.金属学报,2001,37:617) |
| [4] | Hickson M R, Hodgson P D. Mat Sci Tech, 1999,15:85 |
| [5] | Hodgson P D, Hickson M R, Gibbs R K. Mat Sci Forum,1998,284-286:63 |
| [6] | Torizuka S, Umezawa O, Tsuzaki K, Nagai K. Mat Sci Forum, 1998,284-286:225 |
| [7] | Ishikawa T, Nomiyama Y, Yoshikawa H, Imai S, Inoue T.Nippon Steel Technical Report, 1997,75:31 |
| [8] | Yang P, Cui F, Ma S, Wang F. The 4th Inter Conference on HSLA Steels, Liu G Q, Wang F M, Wang Z B,Zhang H T, Metallurgical Industry Press. Eds, et al., Oct.31-Nov.2, China Xi'an,2000:215 |
| [9] | Yang P, Fu Y Y, Cui F E, Sun Z Q. Acta Metall Sin, 2001,37:601(杨平,傅云义,崔风娥,孙祖庆金属学报,2001,37:601) |
| [10] | Yang W, Hu A, Sun Z. Acta Metall Sin, 2000,36:1055(杨王玥,胡安民,孙祖庆,金属学报,2000,36:1055) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%