本文研究了原位SiC颗粒增强MoSi2基复合材料的组织结构和力学性能结果表明:复合材料的组织为t-MoSi2基体上均匀分布β-SiC等轴颗粒,数量很少的球形小孔隙主要分布在SiC颗粒内,SiC颗粒尺寸为2-5μm.复合材料界面为直接的原子结合,无非晶层存在.复合材料的室温维氏硬度、断裂韧性、抗压强度及高温流变应力明显高于单一MoSi2,随着SiC体积分数的增加,维氏硬度、断裂韧性及高温流变应力提高,而抗压强度先增加后减少SiC体积分数从10%增加到45%,KIC从4.34提高到5.71 MPa@m1/2,与单一MoSi2相比提高了25%-46%;1400℃时,σ0.2从20%SiC的230提高到45%SiC的285 MPa,比单一MoSi2提高了98%-146%.
参考文献
| [1] | Vasudevan A K, Petrovic J J. Mater Sci Eng, 1992, 155A:1 |
| [2] | Jeng Y -L, Lavernia E J. J Mater Sci, 1994, 29:2557 |
| [3] | Aikin R M, Jr. Mater Sci Eng, A155, 1992:121 |
| [4] | Henager C H, Jr, Brimhall J L, Brush L N. Mater Sci Eng, 1995, A195:65 |
| [5] | Subrahmanyam J, Rao R M. J Am Ceram Soc, 1995;78(2): 487 |
| [6] | Zhang L Q, Sun Z Q, Zhang Y, Yang W Y. Acta Metal Sin, 1998,34(11): 1205(张来启,孙祖庆,张跃,杨王玥.金属学报,1998;34:1205) |
| [7] | Cotton J D, Kim Y S, Kaufman M J. Mater Sci Eng, 1991;144A: 287 |
| [8] | Hardwick D A, Martin P L, Moores R J. Scripta Mat et Mater, 1992,27:391 |
| [9] | Bhattacharya A K, Petrovic J J. J Am Ceram Soc, 1991;74:2700 |
| [10] | Rice R W, Freiman S W. J Am Ceram Soc, 1981,64:350 |
| [11] | Mitra R, Mahajan Y R, Prasd N E, Chiou W A. Mater Sci Eng, 1997,A225:105 |
| [12] | Wade R K, Petrovic J J. J Am Ceram Soc, 1992,75(6):1682 |
| [13] | Zhang L Q, Sun Z Q, Yang W Y, Zhang Y. Acta Metal Sin, 1999,supplement Ⅱ: s408(张来启,孙祖庆,杨王玥,张跃金属学报,1999年增刊Ⅱ:s408) |
| [14] | Zhou Y. Ceramic materials Science. Harbin: Harbin Institute of Technology Press, 1995:343(周玉.陶瓷材料学.哈尔滨:哈尔滨工业大学出版社,1995:343) |
| [15] | "Mechanical property of Metals ” ed. staff. Mechanical Property of Metals. 2nd ed. Beijing: Mechanical Industry Press, 1982:52(<金属机械性能>编写组编金属机械性能第二版北京:机械工业出版社,1982:52) |
| [16] | Bruckner R J. Noncryst Solids, 1970, 5:123 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%