研究了K417合金在400-850℃同相(IP)和反相(OP)的热机械疲劳(TMF)行为,并且与850℃等温疲劳(IF)性能进行了比较结果发现:K417合金IF和TMF都具有循环硬化特征,IF的循环硬化能力比TMF的要高与等温疲劳寿命相比较,在相同机械应变幅下,TMF的寿命降低,而且同相(IP)的寿命比反相(OP)的寿命更低.SEM断口及断裂纵向剖面检查发现,同相TMF的沿晶开裂是导致其疲劳寿命比反相TMF低的主要原因.
参考文献
| [1] | Vasseur E, Remy L. Mater Sci Eng, 1994,184A: 1 |
| [2] | Henderson P J. Scr Metal Mater, 1996,24:1839 |
| [3] | Marchionni M. Proc Conf Fatigue '93, May, 5 7, 1993,Montreal, Canada, 1993,3:933 |
| [4] | Barmgartner T, Hurta S, Bothe K, Gerold V. Proc Conf Fatigue'90, July, 15-20, 1990, in Honolulu Hawaii. 1990;3:1699 |
| [5] | Guedou J Y, Honnorat Y. ASTM, STP, 1186, 1993,157 |
| [6] | Yan M G. Handbook of engineering material. Beijing:China Standard Press, 1982,2:647(颜鸣皋.工程材料实用手册北京:中国标准出版社,1982;2:647) |
| [7] | Antolovich S D, Liu C, Baur B. Metall Trans, 1981,12(A):437 |
| [8] | Ostergren W J. J Testing Evaluation, 1976,4:327 |
| [9] | Suresh S. Fatigue of Materials(second Edition), Cambridge: Cambridge Press, 1998:138 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%