用光电子能谱和Auger电子能谱等分析手段对纯钼丝表面离子注La后形成的La2O3-Mo阴极表面碳化层的作用机制进行了研究.实验结果表明,碳化层主要起到产生活性物质La的作用,此外还具有贮存和输运活性物质的作用.改变阴极碳化工艺可使La2O3-Mo三极管阴极的寿命由初期的14 h提高到满足实际应用水平(1000 h)的1436.5 h.
参考文献
| [1] | Buxbaum C, Gessinger G. US Pat 4 019 081, 1977 |
| [2] | Buxbaum C, Gessinger G. US Pat 4 083 811, 1978 |
| [3] | Buxbaum C. Boveri Boveri Rev, 1979; 1:43 |
| [4] | Gessinger G, Buxbaum C. High Temp-High Pressures,1978; 10:325 |
| [5] | Goebel D M, Forrester A T, Johnston S. Rev Sci Instrum,1980; 51:1468 |
| [6] | Sreenivasa G R, Dharmadhikari C V, Nigavckar A S. J Vac Sci Technol, 1989; A7: 3269 |
| [7] | Goebel D M, Barber G C. Rev Sci Instrum, 1985; 56:1888 |
| [8] | Zhou M L, Chen Z C, Zhang J X. High Temp-High Pressures, 1994; 26:145 |
| [9] | Zhang J X, Zhou M L, Wang J S, Nie Z R, Zuo T Y. In:Xia Y T ed, '96 Symposium on Materials Ⅲ-2, Beijing:Chemical Industry Press, 1996:585(张久兴,周美玲,王金淑,聂柞仁,左铁镛.见:夏叶涛编,'96中国材料研讨会Ⅲ-2,北京:化学工业出版社,1996:585) |
| [10] | Nie Z R.Ph D Thesis,Central South University of Technology,1997(聂祚仁.中南工业大学博士学位论文,1997) |
| [11] | Wang J S.Ph D Thesis,Beijing Polytechnic University,1999(王金淑.北京工业大学博士学位论文,1999) |
| [12] | Minanov X M,HodakovI O C,Andosn T B,Markov M A ed.Liu H Qtrans.Application of Rare Earth on Catalyst.Beijing:Science Press,1987:13(Minanov X M,HodakovI O C,Andosn T B,Markov MA著.刘恒潜译.稀土在催化中的应用.北京:科学出版社,1987:13) |
| [13] | Zhou M L,Li J,Zuo T Y.Chin J Nonferrous Met,1994;4(2):45(周美玲,李俊,左铁镛中国有色金属学报,1994;4(2):45) |
| [14] | Zhon M L,Li H G,Fu J F.Chin J Nonferrous Met,1987;6:11(周美玲,李汉广,付炯芳.稀有金属材料与工程,1987;6:11) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%