借助于EBSD方法,研究了8个位向B2结构Fe3Al单晶室温拉伸变形时晶体取向的转动.结果表明,无论原始取向如何,在拉伸过程中晶体拉伸轴总会向着〈110〉方向转动,也即〈110〉为稳定取向当晶体拉伸轴转向取向三角形中部的软取向时,晶体表现为几何软化,相应的加工硬化率较低反之,当晶体拉伸轴转向〈001〉-〈101〉对称线时,晶体表现为几何硬化,相应的加工硬化率较高.当拉伸轴处于软取向时,单晶试样的板面转向(111,而当拉伸轴处于硬取向时,板面转向(110).晶体拉伸轴向〈110〉的转动与多晶Fe3Al基合金{001}〈110〉织构相对应;板面向(111的转动与{111}织构对应;板面向(110)的转动则对应{110}〈001〉的剪切织构.
参考文献
| [1] | Orlans-Joliet B, Driver J H, Montheillet F. Acta Metall Mater, 1990; 38:581 |
| [2] | Keh A S. Philos Mag, 1965; 12:9 |
| [3] | Carpay F M A, Chin G Y, Mahajan S, Rubin J J. Acta Metall, 1975; 23:1473 |
| [4] | Yoshimi K, Hanada S. In: Darolia R, Lenvandowski J J,Liu C T, Martin P L, Miracle D B, Nathal M Y eds,Structural Intermetallics, Warrendale, Pennsylvania: The Mineral, Metals & Materials Society, 1993:475 |
| [5] | Mckamey C G, Devan J H, Tortorell P H, Sikka V K. J Mater Res, 1991; 6:1779 |
| [6] | Mao W M, Sun Z Q. Scr Metall Mater, 1993; 29:217 |
| [7] | Sun Z Q, Huang Y D, Yang W Y, Chen G L.Mater Res Soc Symp Proc, 1993; 288:885 |
| [8] | Sun Z Q, Huang Y D, Yang W Y, Mao W M, Chen G L.Acta Metall Sin, 1993; 29:A354(孙祖庆,黄原定,杨王玥,毛卫民,陈国良.金属学报,1993;29:A354) |
| [9] | Sun Z Q, Mao W M. Acta Metall Sin (Eng Lett), 1995; 8:369 |
| [10] | Zheng W W. Yang W Y, Liu Q, Sun Z Q. Acta Metall Sin, 1998; 34:1137(郑为为,杨王玥,刘庆,孙祖庆.金属学报,1998;34:1137) |
| [11] | Hertzberg R W. Fracture Mechanics of Engineering Materials. 2nd ed, New York: Wiley, 1983:88 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%