采用电弧离子镀技术在铸造镍基合金K17和Ni3Al基合金IC-6上沉积Ni-Cr-Al-Y涂层.结果表明,在沉积过程中由于电弧离子镀的"溅射"和"反溅射"效应以及基体和涂层发生互扩散的共同作用下,沉积的Ni-Cr-Al-Y涂层在靠近基体区含有少量基体元素,如Co,Ti和Mo等.K17合金中的Al元素可抑制Cr由涂层向基体扩散.IC-6合金中由于还含有Mo元素,使这种抑制作用进一步增强在1050℃真空热处理时,各元素互扩散能力增强,大量的Cr克服Al和Mo元素的束缚向基体扩散,最终使两种合金上沉积的Ni-Cr-Al-Y涂层中的元素均匀分布.
参考文献
| [1] | Czech N, Juez-Lorenzo M, Kolarik V, Stamm W. Surf Coat Technol, 1998; 108/109:36 |
| [2] | Lih W, Chang E, Wu B C, Chao C H. Surf Coat Technol,1992; 50:277 |
| [3] | Iwamoto H, Sumikawa T, Nishida K, Asano T, Nishida M, Araki T. Mater Sci Eng, 1998; A241:251 |
| [4] | Brandl W, Toma D, Grabke H J. Surf Coat Technol, 1998;108/109:10 |
| [5] | Han Y F, Xing Z P, Chaturvedi M C, Xu Q. Mater Sci Eng, 1997; A239:871 |
| [6] | Brandl W, Grabke H J, Toma D, Krüger J. Surf Coat Technol, 1996; 86/87:41 |
| [7] | Czech N, Schmitz F, Stamm W. Surf Coat Technol, 1994;68/69:17 |
| [8] | Kolomatsev P T, Translated by Ma Z C. Hot-Resistant Diffusion Coatings. Beijing: National Defence Industry Press, 1988:182(КоломьIu евПт著,马志春译.耐热扩散涂层.北京:国防工业出版社,1988:182) |
| [9] | Cai Y L, Zheng Y R. Metallographical Study of Super Alloys. Beijing: National Defence Industry Press, 1986:38(蔡玉林,郑运荣.高温合金的金相研究.北京:国防工业出版社,1986:38) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%