以多元合金系在凝固过程中组元满足的液固界面平衡方程,即组元在液固相中的化学位相等为基础建立了一个反映多元系凝固偏析的简易模型,利用它对多元合金系凝固初期的特征进行了定性描述,并且对某些微量元素在Ni基合金凝固过程中的分配行为进行了计算模拟,得到的结果与实验结果较好地相符.从定性说明和计算模拟的角度,方便地确定出对Ni基合金凝固偏析起决定性作用的微量元素.
参考文献
| [1] | Woodyatt L R, Sims C T. Trans AIME, 1966; 236:519 |
| [2] | Gessinger G H, Bomford M J. Int Met Rev, 1974; 19:51 |
| [3] | Goulette M J. In: Kissinger R D, Deye D J eds, Superalloys 1996, TMS Pittsburg, PA, 1996:3 |
| [4] | Furr D. Adv Mater Proc, 1999; 3:33 |
| [5] | Zhu Y X, Zhang S N, Xu L Y, Bi J, Hu Z Q, Shi C X.In: Superalloys ed, Superalloys 1988, Proc of the Fifth Int Symp, Seven Springs, TMS, PA, 1988:703 |
| [6] | Zhu Y X, Zhang S N, Zhang T X, Zhang J H, Hu Z Q, Xie X S, Shi C X. In: Antolovich S D, Stusrud R W, Mackey R A eds, Superalloys 1992, Proc of the Sixth Int Symp,Seven Springs, TMS, PA, 1992:145 |
| [7] | Cao W D, Kennedy R L. In: Loria E A ed, Superalloys 718, 625, 706 and Various Derivatives, TMS Warrendale,PA, 1997:511 |
| [8] | Holt R T, Wallace W. Int Met Rev, 1976; 21:1 |
| [9] | Tamura M, In; Tien J K, Canlfield Teds, Superalloys, Supercomposites and Superceramics, Academic Press, Boston, 1989:215 |
| [10] | Sung J K, Was G S. Corrosion, 1991; 47:824 |
| [11] | Hu Z Q, Sun W R, Guo S R. Acta Metall Sin (English Lett), 1996; 9:443 |
| [12] | Horton J A, McKamey C G, Miller M K, Cao W D,Kennedy R L. In: Loria E A ed, Superalloys 718, 625,706 and Various Derivatives, TMS Warrendale, PA, 1997:401 |
| [13] | McKamey C G, Garmichael C A, Cao W D, Kennedy R L. Scr Mater, 1998; 38:485 |
| [14] | Laxmanan V. Acta Metall, 1985; 33:1037 |
| [15] | Battle T P, Pehlke R D. Metall Trans, 1990; B21:357 |
| [16] | Yu J Q, Yi W Z, Chen B D, Chen H J. The Phase Diagram of Binary Alloy. Shanghai: Shanghai Science and Technology Press, 1987:249(虞觉奇,易文质,陈邦迪,陈宏鉴.二元合金状态图集.上海:上海科学技术出版社,1987:249) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%