γ'-Fe4N磁粉的超精细结构及结构转变

1.东北大学理学院,沈阳,110006

2.北满钢铁集团物资处,齐齐哈尔,161041

3.东北大学理学院,沈阳,110006

4.北满钢铁集团物资处,齐齐哈尔,161041

5.东北大学理学院,沈阳,110006

HYPERFINE STRUCTURE AND STRUCTURAL TRANSITION OF γ'-Fe4N MAGNETIC POWDER

以铁粉氮化法制备γ'-Fe4N磁粉,用M(o)ssbauer谱学配合X射线衍射方法研究了γ-Fe4N的超精细结构及其变化.结果表明:γ'-Fe4N中存在着三种可区别的Fe原子组态球磨及真空退火处理γ'-Fe4N和α-Fe混合粉末,可生成含α"-Fe16N2的复合氮化铁磁粉.

[1]	Li Z R, Meng Q A, Cao Q J, Sun K, Wei Y N. Acta Phys Sin, 1996; 45:314(李子荣,孟庆安,曹琪娟,孙克,魏玉年.物理学报,1996;45: 314)
[2]	Xue D S, Chen Z Y, Li F S. J Lanzhou Univ (Natural Sciences),1996; 32:49(薛德胜,陈子瑜,李发伸.兰州大学学报(自然科学版),1996;32: 49)
[3]	Koyano T, Lee C H, Fukunaga T, Mizutani U. Mater Sci Forum, 1992; 88-90:809
[4]	Lee P Y, ChenT R, Chin T S. J Alloys Comp, 1995; 22:179
[5]	Shirane G, Takei W J, Ruby S L. Phys Rev, 1962; 126:49
[6]	Nozik A J, Wood J C, Haacke G. Sol State Commun, 1969;7:1677
[7]	Kim K J, Sumiyama K, Shibata K, Suzuki K. Mater Sci Eng,1994; A181:1272
[8]	Koyano T, Takizawa T, Fukunaga T, Mizutani U. Jpn J Appl Phys, 1993; 32:1524
[9]	Kim K J, Sumiyama K, Onodera H, Suzuki K. J Alloys Comp, 1994; 203:169

上一张下一张

计量

作者相关

文章评分