采用燃烧合成工艺,在超高压氮气下,制备了具有较高致密度的AlN/Y2O3陶瓷.研究表明,Al-N2-Y2O3的自蔓延高温合成(SHS)过程为:660℃Al熔化,1000℃Al剧烈挥发并与N2迅速反应形成AlN,放出大量热;当反应温度升至1720℃时,Y2O3与Al2O3形成共晶液相Al5Y3O12,发生液相烧结高温液相烧结使产物的致密度显著提高,但由于其阻碍N2向反应前沿的渗透,产物中残余Al含量增加.随着Y2O3含量的增加,液相烧结作用增强,产物致密度显著提高,抗弯强度及断裂韧性提高.Al-N2-Y2O3体系的SHS致密化主要发生在燃烧波蔓延方向,具有明显的方向性.
参考文献
| [1] | Laurel M.Am Cera Bull,1990; 19(11):1801 |
| [2] | Baik Y,Drew R A L.Key Eng,1996; 122-124:553 |
| [3] | Liu Y C,Zhou H P,Wu Y.J Mater Sci Lett,1999; 189:703 |
| [4] | Zhou H P,Zhou J S.J Inorg Mater,1995; (10):439(周和平,周劲松.无机材料学报,1995;(10):439) |
| [5] | Merzhanov A G.Particulate Materials and Processes:Advances in Powder Metallurgy & Particalate Materials,Vol.6.Princeton,NJ,1992:341 |
| [6] | Zhou H P,Liu Y C,Wu Y.J Chin Cera Soc,1998; 18:517 |
| [7] | Jang G J,Zhuang H R,Li W L.J Inorg Mater,1998; 13:105(江国健,庄汉锐,李文兰.无机材料学报,1998;13:105) |
| [8] | Li Y Q,Qiu T,Xu J.Mater Res Bull,1997; 32:1173 |
| [9] | Costantino M,Firpo J.Mater Res,1991; 6:2397 |
| [10] | Chen K X.Ph D Dissertation,Beijing University of Science and Technology,1997:30(陈克新.北京科技大学博士论文,1997:30) |
| [11] | КуликовИС.ТермодиномикаКарбидовиНитридовЧелябинск:Металлургия,1988:288 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%