用透射电镜研究了Ti细化A357铝合金组织中析出相的形态、组成及其对合金变形、性能的影响.结果表明,Ti细化A357铝合金组织中主要存在着弯曲状的Ti3Si5、直杆状的TiAl3及短棒状的以Al和Ti为主、含Mg和Si的化合物.拉伸变形过程中,析出相阻挡和缠结位错,对合金有一定的强化作用.时效过程中,析出相周围先形成表面无析出区,延长时效时间后该区消失,对合金的拉伸性能造成一定的影响.
参考文献
| [1] | Apelian D, Sigworth G K, Whaler K R. Trans Am Foundrymen's Soc, 1984; 92:297 |
| [2] | Guzowski M M, Sigworth G K, Sentner D A. Metall Trans,1987; 18A: 603 |
| [3] | Mohanty P S, Gruzleski J E. Acta Metall Mater, 1995; 43:2001 |
| [4] | Mohanty P S, Gruzleski J E. Scr Metall Mater, 1994; 31:179 |
| [5] | Backernd L, Gastafson P, Johnson M. Aluminum, 1991; 67:910 |
| [6] | Kaneko J, Sagamata M, Shimamune R. Jpn Foundry Soc Trans, 1991; 10:72 |
| [7] | Marcantonic J A, Mondolfo L F. Metall Trans, 1971; 2:465 |
| [8] | Mondolfo L F. Translated by Wang Z T, Zhang Z L, Zheng X et al. Aluminium Alloys: Structure and Propertys. Beijing:Metallurgical Industry Press, 1988:552(Mondolfo L F著,王祝堂,张振录,郑璇等译.铝合金的组织与性能.北京:冶金工业出版社,1988:552) |
| [9] | Yang D Z. Strengthening Mechanism of Dislocation and Metal. Harbin: Harbin Institute of Technology Publishing House, 1991:182(杨德庄.位错与金属强化机制.哈尔滨:哈尔滨工业大学出版社,1991:182) |
| [10] | Zhu H L, Guo J J, Jia J. Chin J Nonferrous Met, 1997; 7:143(祝汉良,郭景杰,贾均.中国有色金属学报,1997;7(1):143) |
| [11] | Li P Y. PhD Dissertation. Harbin Institute of Technology,1996(李沛勇.哈尔滨工业大学博士学位论文,1996) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%