采用自制的高耐热磷环氧树脂（ED）与脂环族缩水甘油醚环氧树脂（EM）制备了阻燃环氧层压板，并对不同树脂配比的浇铸体及玻璃布层压板性能进行比较分析。结果表明：当m(ED)∶m(EM)为6∶4～7.5∶2.5时，浇铸体的CTI为600，阻燃等级达到UL 94 V-0级；当m(ED)∶m(EM)=6∶4时，环氧层压板的拉伸强度与弯曲强度分别达到530 MPa和610 MPa，冲击强度达到73.5 kJ/m2，且具有优异的电气性能。
A flame retardant epoxy laminate was prepared with self-made high heat resistance phosphoric epoxy resin ED and cycloaliphatic glycidyl ether epoxy resin EM. The properties of the casting resin with different ratio of epoxy resin and the epoxy laminate were analyzed. The results show that when the ratio between ED and EM ranges from 6:4 to 7.5∶2.5, the comparative tracking index (CTI) of the laminate is 600, and the flame retardancy reach UL 94 V-0. When the ratio between ED and EM is 6∶4, the tensile and flexural strength of the epoxy laminate is 530 MPa and 610 MPa respectively, the im-pact strength is 73.5 kJ/m2, and the epoxy laminate has good dielectric property.
参考文献
| [1] | 唐星三;孟烨;刘杰.溴化环氧树脂阻燃剂应用综述与发展展望[J].塑料工业,2011(z1):47-49. |
| [2] | 朱婧文;刁硕;刘成斌.溴代阻燃剂[J].科技信息,2012(25):26,13. |
| [3] | 杨元;李玲.新型含磷阻燃环氧树脂体系的研究进展[J].绝缘材料,2012(2):29-32. |
| [4] | 吴爽;虞鑫海;罗道明.无卤阻燃改性环氧酚醛玻璃布层压板[J].绝缘材料,2011(6):9-11. |
| [5] | Wang XD.;Zhang Q..Synthesis, characterization, and cure properties of phosphorus-containing epoxy resins for flame retardance[J].European Polymer Journal,20042(2):385-395. |
| [6] | 程炎波;李江;何岳山;王碧武;刘渊;王琪;张凯.三聚氰胺氰尿酸盐/磷系阻燃剂协效阻燃环氧树脂覆铜基板的研究[J].绝缘材料,2013(5):9-12,16. |
| [7] | 朱学文.提高覆铜板耐漏电起痕指数的研究[J].绝缘材料,2006(05):7-8,12. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%