目的:研究L80油管在CO2/H2S环境中的腐蚀行为。方法利用扫描电镜(SEM)、EDAX能谱分析L80油管内壁腐蚀产物形貌特征和化学组成,采用高温高压反应釜,以实际油水分离的水样为腐蚀介质进行模拟实验,研究原油含水率、CO2/H2S 分压和温度对 L80油管腐蚀速率的影响规律。结果在CO2/H2S环境中,L80油管内壁呈现明显的局部腐蚀特征,部分表面点蚀坑深度超过100μm,形成FeS、FeCO3等腐蚀产物。随着含水率的增加,L80油管腐蚀速率逐渐增大,含水率为30%时的腐蚀速率为0.0377 mm/a,含水率为100%时的腐蚀速率为0.0952 mm/a。CO2分压不变时,随着 H2S分压的增加,L80钢的腐蚀速率增大,H2S分压为0.04 MPa时的腐蚀速率为0.0377 mm/a,H2S分压为0.3 MPa时的腐蚀速率为0.0952 mm/a;H2S分压不变时,随着CO2分压的增大,L80钢腐蚀速率变化不明显且腐蚀速率较小。随着温度的升高,腐蚀速率先以较大幅度增大,再以较小幅度减小,从40℃增加至100℃时,腐蚀速率由0.0083 mm/a升至0.1264 mm/a,100℃左右时的腐蚀速率最大,120℃对应的腐蚀速率为0.106 mm/a。结论 L80油管在CO2/H2S环境中以均匀腐蚀和局部点蚀为主。L80油管腐蚀速率对H2S分压比CO2分压更敏感,CO2分压增大促使具有良好保护性的FeCO3保护膜的形成,降低了腐蚀速率。温度升高至一定范围,导致碳酸盐等难溶性盐溶解度降低,并覆盖在钢表面形成保护层,从而使腐蚀速率下降。

ABSTRACT:Objective To study the corrosion behavior of L80 tubing in CO2/H2S environment.Methods Scanning elec- tron microscopy (SEM) and EDAX energy spectrum were used to analyze appearance characteristics and chemical compositions of corrosion products, and simulation experiment was conducted using HTHP autoclave and actual water sample after oil/water separation as the corrosive medium, to study the influence law of water cut, CO2/H2S partial pressure and temperature on L80 tubing corrosion rate.Results In CO2/H2S environment, L80 tubing inwall had obvious local corrosion characteristics, the depth of pitting corrosion in part area was more than 100μm,and corrosion products such as FeS,FeCO3 were formed. With the in-crease of water cut, the corrosion rate of L80 tubing gradually increased, the corrosion rate was 0.0377 mm/a when water cut was 30%, the corrosion rate was 0.0952 mm/a when water cut was 100%. When the CO2 partial pressure was constant, with the increase of H2S partial pressure, L80 steel corrosion rate increased; the corrosion rate was 0.0377 mm/a when H2S partial pres-sure was 0.04 MPa; the corrosion rate was 0.0952 mm/a when H2S partial pressure was 0.3 MPa. When the H2S partial pressure was constant, with increasing CO2 partial pressure, the corrosion rate of L80 steel did not significantly change, and the corrosion rate was smaller. With increasing temperature, the corrosion rate firstly significantly increased, and then decreased with a small-er amplitude. The corrosion rate changed from 0.0083 mm/a to 0.1264 mm/a when the temperature increased from 40℃ to 100℃, and the corrosion rate was the largest at about 100℃. The corrosion rate was 0.106 mm/a when the temperature was 120℃.ConclusionL80 tubing had mainly uniform and local corrosion in CO2/H2S environment. The corrosion rate of L80 tubing was more sensitive to H2S partial pressure than CO2 partial pressure. Good FeCO3 protective film was formed when CO2 partial pressure increased, reducing the corrosion rate. When the temperature increased to a certain range, the solubility of car-bonate and other slightly soluble salts was reduced, forming a protective layer on steel surface to decrease the corrosion rate.

参考文献

[1] 王斌;周小虎;李春福;李福德;钟水清.钻井完井高温高压H2S/CO2共存条件下套管、油管腐蚀研究[J].天然气工业,2007(2):67-69.
[2] 王成达;严密林;赵新伟;李平全;王辉.油气田开发中H2S/CO2腐蚀研究进展[J].西安石油大学学报(自然科学版),2005(5):66-70.
[3] 王峰;王立贤;刘智勇;艾池.TP110 TS油管钢在酸性气田环境中的应力腐蚀行为研究[J].表面技术,2015(3):57-62,73.
[4] 万里平;孟英峰;梁发书.油气田开发中的二氧化碳腐蚀及影响因素[J].全面腐蚀控制,2003(2):14-17.
[5] 姚晓;冯玉军.国内外气田开发中管内CO2腐蚀研究进展[J].油气储运,1996(02):12.
[6] 徐士祺;曹宝格;郝上京.温度对油气管道的CO2腐蚀速率的影响研究[J].管道技术与设备,2007(3):32-33.
[7] 朱培珂;邓金根;闫伟;李明洋;吴山;彭程.3Cr钢和13Cr钢在高矿化度CO2环境中的腐蚀行为[J].腐蚀与防护,2014(12):1221-1225.
[8] R. A. Siddiqui;Hussein A. Abdullah.Hydrogen embrittlement in 0.31% carbon steel used for petrochemical applications[J].Journal of Materials Processing Technology,20051/2(1/2):430-435.
[9] J. K. Heuer;J. F. Stubbins.Microstructure analysis of coupons exposed to carbon dioxide corrosion in multiphase flow[J].Corrosion: The Journal of Science and Engineering,19987(7):566-575.
[10] 孙建波;柳伟;路民旭.成分和组织影响钢CO2腐蚀的研究进展[J].中国腐蚀与防护学报,2008(4):246-250.
[11] 陈东;柳伟;路民旭;吴荫顺;侯世颖;陈迎锋.CO2分压对N80钢腐蚀产物膜保护性能的影响[J].北京科技大学学报,2007(3):288-292.
[12] 熊颖;陈大钧;王君;张启根.油气开采中H2S腐蚀的影响因素研究[J].石油化工腐蚀与防护,2007(6):17-19,48.
[13] 张清;李全安;文九巴;白真权.H2S分压对油管钢CO2/H2S腐蚀的影响[J].腐蚀科学与防护技术,2004(6):395-397.
[14] 艾志久;范钰伟;赵乾坤.H2 S对油气管材的腐蚀及防护研究综述[J].表面技术,2015(9):108-115.
[15] 闫伟;邓金根;董星亮;张春阳;李立宏;李晓蓉.油管钢在C02/H2S环境中的腐蚀产物及腐蚀行为[J].腐蚀与防护,2011(3):193-196.
[16] 吕旺燕;于全成;王振尧;苏伟.P265GH低合金钢在模拟污染大气环境中的腐蚀行为[J].装备环境工程,2015(4):66-71.
[17] 刘巾军.铝合金在模拟海岛环境中腐蚀产物的红外光谱研究[J].装备环境工程,2015(4):124-128.
[18] 邢青;郭为民;陈祥曦;范林;龚利华;杨超.铜合金在模拟深海低温条件下的电偶腐蚀行为研究[J].装备环境工程,2015(2):1-5,24.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%