使用熔融淬冷法制备了Er3+掺杂Ge-Ga-S-CsBr硫卤玻璃，研究了其在1550 nm激光激发下的上转换发光特性，观察到强的波长中心位于525和545 nm绿色发光及弱的中心波长位于660 nm红色发光，也观察到了中心波长分别位于810和980 nm的红外上转换发光。基于泵探光功率关系和能级寿命测试研究了发光机理，发现中间态能级寿命的延长是上转换发光效率增强的根本原因。使用全光谱光源测试了Si太阳能效率，当使用上转换发光层时，太阳能电池平均效率从7.28%上升至7.32%。结果显示所探索的稀土掺杂硫卤玻璃有望应用于硅太阳能电池效率增强领域。
Er3+ doped Ge-Ga-S-CsBr chalcohalide glasses were fabricated by melt-quenching method. The proper-ties of upconversion luminescence under the excitation of 1550 nm laser were investigated. Strong green emissions centered at 525 nm and 545 nm, and weak red emission centered at 660 nm, were observed, along with near infrared emission bands centered at 810 nm and 980 nm. The up-conversion fluorescence was contributed to multi-photon involved process. The Si solar cell efficiency slightly increased from 7.28% (without upconversion layer) to 7.32% (using Er3+ doped 0.9(Ge25Ga10S65)-0.1CsBr glass as upconversion layer). The results show that the investigated Er3+-doped chalcohalide glasses has a potential application for the enhancement of Si solar cell efficiency.
参考文献
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%