分别以Y2O3-Al2O3(YA)和Y2O3-MgO(YM)为烧结助剂，采用气压烧结工艺制备了Si3N4/SiC陶瓷，研究了两种不同的烧结助剂对陶瓷的力学和摩擦性能的影响。研究结果表明：添加不同种类的烧结助剂对制备陶瓷的相对密度、抗弯强度、断裂韧性、硬度、摩擦系数和磨损率影响很大；与添加烧结助剂YM相比较，添加烧结助剂YA的Si3N4/SiC陶瓷在烧结过程中表现出了更好的烧结性能，得到的陶瓷样品最终显示了更好的力学和摩擦性能，尤其是SiC添加量为20wt%的Si3N4/SiC陶瓷。这主要归因于烧结助剂YA的添加使Si3N4/SiC陶瓷呈现出了更高的相对密度，获得的晶粒长径比更小。
Two compositions of the Y2O3-Al2O3 (YA) and Y2O3-MgO (YM) systems were chosen to investigate the ef-fect of sintering additive composition on the mechanical and tribological properties of gas pressure sintered Si3N4/SiC ceramics. The relative density, flexural strength, fracture toughness, hardness, coefficient of friction and wear rate were verified to depend substantially on the sintering additive composition. Compared with YM, the Si3N4/SiC ceramics with YA exhibit superior sinterability and show preferable mechanical and tribological properties, especially for the Si3N4/SiC ceramics with 20wt%SiC addition. These properties can be primarily attributed to the higher relative den-sity and the grain size with smaller aspect ratio.
参考文献
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%