研究了再结晶温度以下不同温度的双相钢B340/590DP的拉深性能.数值模拟显示B340/590DP钢随着温度的上升拉深过程中材料的等效应力是下降的，但材料的实际拉深性能在300℃以内并未随温度的升高而改善，在温度超过400℃以后材料的拉深性能明显改善，在500℃时材料的拉深极限系数由常温的0．52降为0．5.实验结果表明，当温度加热至400℃以上时，板料的实际成形性能提高，拉深试样的厚度分布更加均匀.
The drawing property of the dual phase steel B340/590DP below recrystallization temperature was studied. A numerical simulation showed that the equivalent stress decreases with rise of temperature in drawing, however the actual deep drawing properties within 300 ℃ do not improve with rise of the temperature, while the drawing properties are improved significantly when temperatures are over 400℃. The drawing limit coefficient at 500℃drops to 0. 5 from 0. 52. The experimental results showed that the actual forming property is improved above 400 ℃. The drawing sample thickness distribution is more uniform.
参考文献
| [1] | 蔡玉俊;王玉广;李国和;孙奇涵.超高强度钢板热冲压成形CAE技术的研究现状与发展趋势[J].锻压技术,2011(4):7-11. |
| [2] | 金榕 .冷轧双相钢工艺参数及组织性能的研究[D].南京理工大学,2008. |
| [3] | 王恩博 .双相钢温成形中微观组织研究和试验分析[D].江苏大学,2012. |
| [4] | 曹志福;陈炜;王祥.镁合金十字杯形件温拉深成形工艺研究[J].热加工工艺,2013(1):121-123. |
| [5] | 方刚;马鸣图;Dongun Kim;金庆生;宋磊峰;蒋松蔚.三种强度级别的双相钢成形性能研究[J].中国工程科学,2014(1):66-70. |
| [6] | 廖海洪;梁敏洁.20CrMnTi钢温变形时组织与性能变化研究[J].热加工工艺,2001(2):47-49. |
| [7] | 郭玉琴;王帅;朱新峰;李富柱.双相钢温拉伸的后继屈服行为[J].塑性工程学报,2015(4):141-145. |
| [8] | 陈小芳;扶名福;袁志军.DYNAFORM数值模拟技术在汽车覆盖件成形中的应用[J].热加工工艺,2009(11):89-92. |
| [9] | Chu WY.;Qiao LJ.;Wang YB..Interaction between blue brittleness and stress corrosion cracking[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,20002(2):250-254. |
| [10] | 刘倩 .成形速度对B340/590DP板料冲压成形性能影响的研究[D].华中科技大学,2013. |
| [11] | 赵阳 .Docol1200M超高强钢板温拉胀成形性能研究[D].重庆理工大学,2013. |
| [12] | 陈志峰 .双相钢成形性能及温拉伸组织演变研究[D].江苏大学,2014. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%