研究了TC4钛合金阳极氧化及与PTFE制备的复合涂膜的耐摩擦磨损性能,结果表明,采用恒电位阳极氧化法,在H2SO4电解液体系中影响TC4钛合金氧化多孔膜孔径尺寸、均匀性及膜厚的主要因素是H2SO4浓度、氧化电压和温度;时间对膜孔影响较小,氧化到一定时间后膜厚不再增大;当H2SO4浓度为0.5～0.8 mol/L、电压120～130 V、温度-5～5℃条件下,氧化120 min,膜厚约为12μm,孔径约150～400 nm,膜孔分布均匀;试验结果表明,钛合金阳极氧化-PTFE复合涂层摩擦系数约为0.22,而TC4钛合金基体摩擦系数约为0.44,比钛合金基体降低了约50％,磨损量比TC4钛合金基体降低约70％,显著提高了自润滑减摩、耐磨性能.
参考文献
| [1] | 曹辉亮,刘宣勇,丁传贤.医用钛合金表面改性的研究进展[J].中国材料进展,2009(09):9-17. |
| [2] | 付艳艳,宋月清,惠松骁,米绪军.航空用钛合金的研究与应用进展[J].稀有金属,2006(06):850-856. |
| [3] | 李文平.钛合金的应用现状及发展前景[J].轻金属,2002(05):53-55. |
| [4] | 屠振密,朱永明,李宁,胡会利,曹立新.钛及钛合金表面处理技术的应用及发展[J].表面技术,2009(06):76-78,86. |
| [5] | 林修洲,郑健峰,林志君,朱旻昊.TC4钛合金微弧氧化涂层的制备与微动磨损性能研究[J].航空材料学报,2009(02):43-47. |
| [6] | LIN Xiu-zhou,ZHU Min-hao,ZHENG Jian-feng,LUO Jun,MO Ji-liang.Fretting wear of micro-arc oxidation coating prepared on Ti6Al4V alloy[J].中国有色金属学报（英文版）,2010(04):537-546. |
| [7] | 张毅斌.船用钛合金表面改性技术研究进展[J].材料开发与应用,2009(05):70-74. |
| [8] | A. L. Yerokhin;X. Nie;A. Leyland;A. Matthews .Characterisation of oxide films produced by plasma electrolytic oxidation of a Ti-6Al-4V alloy[J].Surface & Coatings Technology,2000(2/3):195-206. |
| [9] | 吴宏亮,缪强,徐一,蒋穹.Ti6Al4V合金表面Ti（C,N）改性层的摩擦性能[J].金属热处理,2012(01):53-56. |
| [10] | M. I. De Barros;L. Vandenbulcke;J. J. Bléchet .Influence of diamond characteristics on the tribological behaviour of metals against diamond-coated Ti-6Al-4V alloy[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2001(1/2):68-78. |
| [11] | Grogler T.;Horner A.;Rosiwal SM.;Singer RF.;Zeiler E. .Microwave-plasma-CVD of diamond coatings onto titanium and titanium alloys[J].Surface & Coatings Technology,1998(1/3):1079-1091. |
| [12] | Barros M.I.;Vandenbulcke L. .Plasma-assisted chemical vapor deposition process for depositing smooth diamond coatings on titanium alloys at moderate temperature[J].Diamond and Related Materials,2000(11):1862-1866. |
| [13] | Yijun Shi;Xin Feng;Huaiyuan Wang;Xiaohua Lu .The effect of surface modification on the friction and wear behavior of carbon nanofiber-filled PTFE composites[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2008(11/12):934-939. |
| [14] | 王元清,关建,张勇,杨璐.不锈钢构件螺栓连接摩擦面抗滑移系数试验[J].沈阳建筑大学学报（自然科学版）,2013(05):769-774. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%