为验证含硅大分子相容剂在无卤阻燃体系中的协效阻燃作用,首先,以马来酸酐、硅橡胶与聚乙烯为原料,通过熔融接枝共聚制备了新型含硅阻燃大分子相容剂;然后,利用氢氧化铝、氢氧化镁和含硅大分子相容剂复配协同阻燃聚乙烯复合材料;最后,探讨了含硅大分子相容剂对复合材料极限氧指数、锥形量热参数、拉伸性能以及微观结构的影响.结果表明:与聚乙烯接枝马来酸酐相比,含硅大分子相容剂含量为10wt％时可使无机阻燃剂在基体树脂中分散较好;随着大分子相容剂含量的增加,复合材料的拉伸强度上升而断裂伸长率下降,极限氧指数提高至34.0％,燃烧时的热释放速率峰值和热释放总量均明显下降,说明含硅大分子相容剂除了能够在该复合材料中起到良好的相容作用外,还可以发挥较好的协效阻燃作用.
参考文献
| [1] | Chang, ZH;Guo, F;Chen, JF;Yu, JH;Wang, GQ.Synergistic flame retardant effects of nano-kaolin and nano-HAO on LDPE/EPDM composites[J].Polymer Degradation and Stability,20077(7):1204-1212. |
| [2] | Carpentier F.;Le Bras M.;Delobel R.;Foulon M.;Bourbigot S..Charring of fire retarded ethylene vinyl acetate copolymer - magnesium hydroxide/zinc borate formulations[J].Polymer Degradation and Stability,20001(1):83-92. |
| [3] | 李明.塑料阻燃剂的研究进展[J].上海化工,2006(06):27-31. |
| [4] | Ye, L.;Miao, Y.;Yan, H.;Li, Z.;Zhou, Y.;Liu, J.;Liu, H..The synergistic effects of boroxo siloxanes with magnesium hydroxide in halogen-free flame retardant EVA/MH blends[J].Polymer Degradation and Stability,20134(4):868-874. |
| [5] | 于杨;刘立柱;翁凌;崔巍巍;朱兴松.Mg（OH）2对苯并噁嗪-环氧树脂复合材料阻燃性的影响[J].复合材料学报,2014(5):1167-1172. |
| [6] | 刘继纯;常海波;李晴媛;陆昶;潘炳力;杜西刚.Mg（OH）2/聚苯乙烯复合材料的阻燃机制[J].复合材料学报,2012(5):32-40. |
| [7] | Esin Ibibikcan;Cevdet Kaynak.Usability of three boron compounds for enhancement of flame retardancy in polyethylene-based cable insulation materials[J].Journal of fire sciences,20142(2):99-120. |
| [8] | 王朝辉;李蕊;赵娟娟;贺海.两种新型无机复合阻燃改性沥青的流变性能及其阻燃机制[J].复合材料学报,2014(6):1597-1603. |
| [9] | 石志想;傅仁利;何兵兵;李冉;俞晓东.无机填料对环氧模塑料导热和阻燃性能的影响[J].复合材料学报,2011(6):8-13. |
| [10] | Liu, J.;Zhang, Y..Effect of ethylene-acrylic acid copolymer on flame retardancy and properties of LLDPE/EAA/MH composites[J].Polymer Degradation and Stability,201112(12):2215-2220. |
| [11] | Zaihang Zheng;Huimin Sun;Wenjie Li.Co-microencapsulation of Ammonium Polyphosphate and Aluminum Hydroxide in Halogen-Free and Intumescent Flame Retarding Polypropylene[J].Polymer Composites,20144(4):715-729. |
| [12] | 刘继纯;于卓立;陈梁;罗洁;郑喜俊;潘炳力.Mg（OH）2-Al（OH）3-微胶囊红磷/高抗冲聚苯乙烯无卤阻燃复合材料[J].复合材料学报,2013(4):35-43. |
| [13] | 迟晓红;俞利;郑杰;高俊国;张晓虹.蒙脱土/聚丙烯复合材料结晶形态及耐电树枝化特性[J].复合材料学报,2015(1):76-84. |
| [14] | 马宝红;刘红;姜国发;王岩;鲍文波;高广刚.耐温125℃紫外光交联低烟无卤阻燃绝缘材料的研制[J].电线电缆,2012(4):27-31. |
| [15] | Genovese A;Shanks RA.Structural and thermal interpretation of the synergy and interactions between the fire retardants magnesium hydroxide and zinc borate[J].Polymer Degradation and Stability,20071(1):2-13. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%