采用将火焰热喷涂技术、自蔓延高温合成技术及快速冷却凝固技术结合在一起的自反应淬熄法,制备了以尖晶石型钡铁氧体为主的空心微珠,然后分别以3,7和15℃·min-13种升温速率将其加热到1100℃、保温4h后再冷却至室温,通过扫描电镜(SEM),X射线衍射(XRD)和矢量网络分析仪等手段,研究了3种升温速率下空心微珠形貌和吸波性能的变化.结果表明:未热处理时,空心微珠主要由Al2O3,Fe2O3,Fe3O4,BaFe2O4组成,表面无明显晶粒出现,最低反射率为-2 dB;3℃·min-慢速升温条件下,空心微珠物相主要由Fe2O3,BaFe12O19,BaAl12O19和Al2O3组成,表面出现了典型的六角晶型,反射率有3个极值,最低反射率为-16.5 dB,低于-10 dB的吸收带宽为2.2GHz;7 ℃·min-1中速升温条件下,物相组成为Fe2O3,BaFe12O19,BaAl12 O19,Al2O3和Fe3O4,微珠表面以片状晶为主,最低反射率为-6.5dB; 15℃·min-1快速升温条件下,由于晶体生长和受扩散控制的固相反应不充分,物相组成中出现了Ba0.83 Fe11O17.33和BaFe13.2O20.8中间相,空心微珠表面主要为等轴晶,最低反射率为-3.9 dB.慢速升温时钡铁氧体空心微珠吸波性能优于中速和快速升温条件.
参考文献
| [1] | 石轩,蒲永平,刘丹.微波水热法合成BaFe12O19磁性粉体[J].人工晶体学报,2013(01):134-137,143. |
| [2] | 左锦中,江静华,马爱斌,王泽华,林萍华.粉煤灰空心微珠的Co-Ni-P化学镀及镀层的吸波性能[J].材料保护,2011(04):15-18. |
| [3] | Geleil AS;Hall MM;Shelby JE .Hollow glass microspheres for use in radiation shielding[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2006(6/7):620-625. |
| [4] | Schmitt ML;Shelby JE;Hall MM .Preparation of hollow glass microspheres from sol-gel derived glass for application in hydrogen gas storage[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2006(6/7):626-631. |
| [5] | Liqiang Xu;Wanqun Zhang;Qing Yang .A novel route to hollow and solid carbon spheres[J].Carbon: An International Journal Sponsored by the American Carbon Society,2005(5):1090-1092. |
| [6] | Wang ZL.;Yin JS. .Graphitic hollow carbon calabashes[J].Chemical Physics Letters,1998(1/2):189-192. |
| [7] | Yukito Oda;Katsuya Fukuyama;Keiko Nishikawa;Seitaro Namba;Hideaki Yoshitake;Takashi Tatsumi .Mesocellular Foam Carbons:Aggregates of Hollow Carbon Spheres with Open and Closed Wall Structures[J].Chemistry of Materials,2004(20):3860-3866. |
| [8] | 苑慧萍,李志念,赵旭山,王树茂,刘晓鹏,蒋利军.热处理对Nd-Mg-Ni储氢合金结构和性能的影响[J].稀有金属,2013(03):341-347. |
| [9] | 魏丽,张恒,李树索,马岳,宫声凯.热处理对一种Ni3Al基单晶合金组织的影响[J].稀有金属,2012(02):178-183. |
| [10] | 兰银辉,高学绪,乔袆,高静,包小倩.自蔓延高温合成钡铁氧体的研究[J].材料导报,2007(z1):333-335. |
| [11] | 雷军,戴红莲,毛恩亮,肖峰,李世普.球形纳米BaFe12O19的制备及表面改性[J].硅酸盐学报,2010(12):2289-2295. |
| [12] | 陈明,程旭东,毛昉.热处理对钡铁氧体空心微球的结构及静磁性能的影响[J].过程工程学报,2008(05):1018-1021. |
| [13] | 闫梨,黄英,王艳丽,李玉青.焙烧对溶胶-凝胶自蔓延燃烧法制备的钡铁氧体粉体相成分与磁性能的影响[J].磁性材料及器件,2007(04):37-40. |
| [14] | 陈晓东,王桂芹,段玉平,李伟平,刘顺华.壳-芯型复合陶瓷材料的制备及其电磁特性[J].无机材料学报,2007(03):456-460. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%