在 IF 钢的生产过程中，退火是非常关键的工艺环节。针对酒钢 CSP 生产的 Ti-IF 钢进行研究，分析了在罩式退火工艺条件下，罩式退火工艺对 Ti-IF 钢组织与性能的影响。结果表明：退火温度从680℃上升到750℃保温2 h，试样抗拉强度从284下降到268 MPa，屈服强度从114下降到96 MPa，屈强比从0．40降低到0．36，伸长率从44．3％提高到47％，塑性应变比 r 90值从2．22升高到2．60。
Annealing is the key limit in the productive process of IF steel.Focusing on the TI-IF steel produced by CSP process in JiuSteel,the effect of batch type annealing process on microstructure and properties of Ti-IF steel is investigated.The results indicate that when the annealing temperature increases from 680 ℃ to 750 ℃ within 2 h, tensile strength reduces from 284 to 268 MPa,yield strength reduces from 114 MPa to 96 MPa ,yield ratio decrea-ses from 0.40 to 0.36,elongation increases from 44.25% to 47% and r 90 increases from 2.22 to 2.60.
参考文献
| [1] | 康永林.现代汽车板的质量控制与成形性[M].北京:冶金工业出版社,1999.,1999. |
| [2] | 潘秀兰,王艳红,梁慧智,冯士超.国内外超低碳IF钢炼钢工艺分析[J].鞍钢技术,2009(01):6-9. |
| [3] | Akbari G H,Sellars C M,Whiteman J A .Mierostrueture de-velopment during warm rolling of an IF steel[J].Actamateri-alia,1997,45(12):50.,1997. |
| [4] | 高攀,田志红,崔阳,胡帅,李永林,朱立新.IF钢非稳态浇铸铸坯洁净度分析[J].钢铁,2012(07):31-35. |
| [5] | 徐海卫,于洋,李飞,朱国森,李本海.IF钢热轧薄板边部翘皮缺陷的产生原因及机制[J].钢铁,2012(09):53-56. |
| [6] | 侯自勇,许云波,吴迪,王国栋.一种高Nb-IF冷轧薄板钢的组织性能及织构[J].钢铁研究学报,2012(05):47-52,62. |
| [7] | 水恒勇,赵爱民,汪志刚,王纯,苏岚.再结晶退火温度对高强IF钢组织性能及织构的影响[J].轧钢,2012(02):8-11. |
| [8] | 穆海玲,李清燕,裴新华,赵骧.热轧和卷取温度对IF钢织构的影响[J].轧钢,2012(03):17-19. |
| [9] | 王昭东,郭艳辉,赵忠,孙大庆.应用铁素体区热轧工艺开发超低碳热轧深冲板[J].东北大学学报（自然科学版）,2005(08):747-750. |
| [10] | 刘战英,周满春,王涛,刘相华,王国栋.IF钢铁素体区热轧工艺参数对深冲性能的影响[J].钢铁研究学报,2007(04):44-46,94. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%