带钢横向厚度控制不均，会使带钢在退火过程中产生横向温度差异和横向张应力分布差异，而横向温度和横向张应力分布存在差异会使带钢横向各位置处产生纵向延伸不均，进而导致退火带钢板形不良。以实际生产过程中带钢横向厚度控制不均的典型现象为切入点，分析带钢横向厚度不均对退火板形的影响，对分析和改进退火板形有一定的指导意义。
The non‐uniform control of transverse thickness of the strip would cause the transverse temperature and the distribution of the transverse tension stress affected in annealing process ,w hile the transverse temperature and transverse tension stress distribution differences would make the strip has uneven longitudinally extending in trans‐verse direction ,which results in poor annealing strip shape .Based on the typical uneven phenomenon of the trans‐verse thickness control of strip in actual production process ,the influence of transverse thickness unevenness on an‐nealing strip flatness was analyzed ,providing certain significance to the analysis and improvement of annealing shape .
参考文献
| [1] | 张清东,常铁柱,戴江波,王文广.连退线上带钢张应力横向分布的有限元仿真[J].北京科技大学学报,2006(12):1162-1166. |
| [2] | 戴江波,张清东,陈先霖,吴彬,邹玉贤.连续退火炉内带钢的热态大挠度变形分析[J].机械工程学报,2003(12):71-74. |
| [3] | 叶玉娟,周旭东,李俊,胡广魁.连续退火炉内带钢跑偏和热瓢曲研究进展[J].轧钢,2009(04):35-38. |
| [4] | 李文科;许永贵;赵永生 .CAPL 均热室供热制度对炉温及带钢热瓢曲的影响[J].钢铁,1996,31(10):45. |
| [5] | 令狐克志,乔建军,王洋,朱国森,刘光明.带钢连退热瓢曲与初始板形关系仿真与实践[J].钢铁,2012(02):58-61. |
| [6] | 徐鹤贤.冷轧钢带板形及其控制工艺探讨[J].特钢技术,2000(2):14. |
| [7] | 马云龙,高振宇,罗理,林刚,刘立新,王铁.硅钢在连续退火机组浪形缺陷的控制[J].鞍钢技术,2013(03):49-52. |
| [8] | 梁俊杰 .连退炉中冷轧板瓢曲产生原因分析及对策研究[D].华中科技大学,2011. |
| [9] | 黄夏兰,彭俊.连续退火炉内带钢热瓢曲的产生机理及控制方法简介[J].世界钢铁,2002(05):14-17,28. |
| [10] | 彭俊 .薄板连续退火机组热瓢曲机理与控制方法研究[D].东北大学,2009. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%