利用光学显微镜对430铁素体不锈钢板坯表面振痕深度和形貌进行观察.结果表明:利用金相法测量振痕深度,测量的结果可以达到很高的精度.430连铸坯表面边部振痕深且紊乱,中部振痕浅、分布比较均匀.上表面边部和中部振痕深度平均值分别为320.847 6 μm和247.886 μm;下表面边部和中部振痕深度平均值为301.753 μm和221.753 6 μm. 430不锈钢深振痕谷底有微裂纹和偏析带存在.通过优化结晶器的振频、振幅及保护渣黏度等工艺参数可以显著减小430板坯的振痕深度.
参考文献
| [1] | 付邦豪,陈超,成国光,潘吉祥,李岩,潘伟.430不锈钢冶炼过程的夹杂物[J].钢铁,2012(01):40-43. |
| [2] | 王建新,陈兴润,潘吉祥.430不锈钢热轧板夹杂物分析[J].连铸,2013(02):38-41. |
| [3] | Hefting G;Odnevall Wallinder I;LeygrafC.Corrosion-induced release of chromium and iron from ferritic stainless steel grade AISI 430 in simulated food contact[J].Journal of Food Engineering,2008(87):291. |
| [4] | Jun-xian Liu,Yong-jun Zhang,Jing-tao Han.Test research on sticking mechanism during hot rolling of SUS 430 ferritic stainless steel[J].矿物冶金与材料学报,2010(05):573-578. |
| [5] | 邢丽娜.304不锈钢连铸板坯振痕形成及控制[J].山西冶金,2007(02):27-28,34. |
| [6] | 张林涛,邓安元,王恩刚,赫冀成.连铸坯表面振痕的形成及影响因素[J].炼钢,2006(04):35-39. |
| [7] | Klaus Schwetfeger.Depth of oscillation marks forming in continuous casting of steel[J].Metallurgical and Material Transaction B,2000(31B):802. |
| [8] | 马宁博,雷作胜,金小礼,任忠鸣.304L不锈钢连铸坯表面振痕形貌及宏观偏析成因分析[J].特种铸造及有色合金,2009(09):837-841. |
| [9] | 金小礼,雷作胜,任忠鸣,邓康,钟云波.连铸坯振痕形成机理及电磁控制技术[J].上海金属,2007(01):15-20. |
| [10] | 王昌绪,王新华,王万军,张立.提高连铸结晶器振动频率、减少振幅改善铸坯质量的研究[J].钢铁,2003(01):19-21,42. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%