采用金相显微镜、复型萃取、SEM、TEM对析出物的形貌、尺寸、数量进行统计分析,并利用Gleeble-1500热模拟试验机,系统研究了含Nb-Ti微合金钢第三脆性区的热塑性.结果表明:温度在950～700℃范围内时,断面收缩率最小为25.7％.析出物以TiN、Nb(CN)为主,950℃时粒子尺寸在50nm左右.随着温度的降低,粒子数量密度由51个/μm2增加到580个/μm2,尺寸随之减小.975℃的抗拉强度及临界应力分别为58.3、61.0 MPa.975℃以上,临界应力小于抗拉强度,不易发生沿晶断裂.975℃以下时,晶粒变形临界应力大于抗拉强度,产生沿晶断裂.
参考文献
| [1] | Thomas B G;Brimacombe J K;Samarasekera I V .The Formation of Panel Cracks in Steel Ingots:A State of the Art Review[J].ISS Transactions,1986,7(10):7. |
| [2] | Kim K;Han H N;Yeo T et al.Analysis of Surface and Internal Cracks in Continuous Cast Beam Blank[J].Ironmaking and Steelmaking,1997,24(03):249. |
| [3] | 蔡兆镇,朱苗勇.溶质偏析对连铸坯凝固前沿裂纹敏感性影响的研究[J].铸造技术,2009(11):1396-1401. |
| [4] | 朱正海,仇圣桃,李广敏,廖鹏,夏文勇.连铸过程铸坯应变对碳氮化铌析出行为的影响[J].炼钢,2009(06):53-55. |
| [5] | Manohar P A;Dunne D P;Chnadra T et al.Grain Growth Prediction Microalloyed Steels[J].ISIJ International,1996,36(02):194. |
| [6] | Andrews K W .Empirical Formation for the Calculation of Some Transformation Temperature[J].Journal of the Iron and Steel Institute,1965,6(07):721. |
| [7] | 岳尔斌,仇圣桃,干勇.低合金高强度钢奥氏体相中碳氮化物的析出模型[J].钢铁研究学报,2006(08):49-52. |
| [8] | Turkdogan E T .Causes and Effects of Nitride and Carbonitride Precipitation During Continuous Casting[J].Iron & Steelmaker,1989,16(05):61. |
| [9] | P.A.Manohar .Continuous Cooling Transformation Behaviour of High Strength Microalloyed Steels for Linepipe Applications[J].ISIJ International,1998(7):766-774. |
| [10] | 解家英,王凤琴,宁林新,王卫华.X80管线钢中Nb元素析出规律的研究[J].钢铁研究学报,2010(09):38-42. |
| [11] | 王岩,赵爱民,陈银莉,唐获,左碧强.高铌X80管线钢连铸过程中微合金元素的析出行为[J].钢铁,2011(05):64-68. |
| [12] | 雍歧龙.钢铁材料中的第二相[M].北京:冶金工业出版社,2006 |
| [13] | 刘新宇 .微合金化钢连铸坯碳氮化物的析出及高温延塑性的研究[D].北京科技大学,2000. |