为研究深冲织构的演变规律，利用OM、TEM和XRD等技术研究了热轧卷取温度对微碳深冲DP钢组织、性能与织构的影响。结果表明，热轧板主要由铁素体＋珠光体构成，随卷取温度升高，铁素体晶粒略增大，伸长率逐渐上升；热轧板中钼基碳化物的最佳析出温度为700℃；与650和750℃相比，700℃卷取后的退火板能获得较高体积分数（4.0%）马氏体与较细（11.7μm）铁素体的组织特征，同时拥有最强的〈111〉//ND纤维织构和最弱的{001}〈110〉织构，使得其抗拉强度达到455 MPa，塑性应变比r值达1.5。
In order to study the charge rule of texture on deep-drawing DP steel,effect of hot-rolled coiling temperature on microstructure,properties and textures of micro-carbon deep drawing DP steel were studied by OM,TEM and XRD technical. The research shows that:microstructure of hot-rolled plates is mainly composed of ferrite and pearlite. With the increasing of coiling temperature,the grain size of ferrite increased slightly,and elongation of hot-rolled plate en-hanced gradually. The optimum precipitation temperature of Mo-based carbide in hot-rolled plate is 700℃. A higher vol-ume fraction (4%) of martensite and finer (11.7μm) ferrite observed in annealed sheet on 700℃coiling compared with 650 and 750 ℃. Meanwhile,the strongest〈111〉//ND fiber texture and weakest {001}〈110〉texture achieved in an-nealed sheet. The tensile strength and r value of annealed sheet on 700℃ coiling reach to 455 MPa and1.5,respectively.
参考文献
| [1] | Seong-Ho Han;Shi-Hoon Choi;Jae-Kwon Cho;Hwan-Goo Seong;In-Bae Kim.Effect of hot-rolling processing on texture and r-value of annealed dual-phase steels[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20107/8(7/8):1686-1694. |
| [2] | Hiromi Yoshida;Kaneharu Okuda;Hidetaka Kawabe.Effect of niobium addition on the texture formation of high strength cold-rolled low carbon steel sheets[J].Materials Science Forum,2007Pt.1(Pt.1):425-430. |
| [3] | Ohjoon Kwon;Kyooyoung Lee;Gyosung Kim.New Trends in Advanced High Strength Steel Developments For Automotive Application[J].Materials Science Forum,2010Pt.1(Pt.1):136-141. |
| [4] | 刘清梅;赵素兰;王铭君;赵瑾.国际钢铁企业高强度冷轧汽车板研发实践[J].轧钢,2014(6):44-48. |
| [5] | 郑跃强;唐兴昌.罩式退火工艺对 Ti-IF 钢组织与性能的影响[J].中国冶金,2015(9):22-26. |
| [6] | 惠亚军;于洋;王林;王畅;陈斌;陈瑾.钛微合金化IF钢第二相粒子应变诱导析出行为[J].钢铁,2016(1):82-89. |
| [7] | 左军;张开华;常军;杨金成;王平莉.Nb+Ti IF钢冷轧板罩式炉退火工艺研究[J].钢铁,2008(4):105-108. |
| [8] | 邹明;唐兴昌;郑跃强;徐荣嬛.退火工艺对DC04汽车板再结晶组织和织构的影响[J].中国冶金,2016(4):51-56. |
| [9] | 彭兆丰;吝章国;谷凤龙;何方;李守斌.邯钢600 MPa级冷轧双相钢的连退工艺[J].中国冶金,2014(4):31-35. |
| [10] | S. F. MEDINA;J. E. MANCILLA.Static Recrystallization Modelling of Hot Deformed Steels Containing Several Alloying Elements[J].ISIJ International,19968(8):1070-1076. |
| [11] | A. K. De;S. Vandeputte;B. C. De Cooman.Kinetics of strain aging in bake hardening ultra low carbon steel-- a comparison with low carbon steel[J].Journal of Materials Engineering and Performance,20015(5):567-575. |
| [12] | 叶洁云;赵征志;张迎晖;齐亮.硅和铬对超高强双相钢组织和性能的影响[J].钢铁,2015(3):78-83. |
| [13] | 鲍成人;李众;谭谨峰;邸洪双;潘恩宝.连续退火冷却速率对热镀锌双相钢DP780屈服平台的影响[J].钢铁,2010(5):81-83,92. |
| [14] | Seong Ho Han;Yeon Sang Ann;Kwang Geun Chin.The Effect of Mo and Cr addition on the Deep Drawability of Dual Phase Steel Sheets[J].Journal of the Korean Institute of Metals and Materials,200811(11):683-694. |
| [15] | 赵新凯;刘江伟;刘西峰;鞠伟.传统流程冷轧低碳铝镇静钢深冲性能分析[J].钢铁,2010(8):85-89. |
| [16] | 吕庆功;李成明;倪爱娟.微碳深冲钢板中非{111}织构的工序演变[J].材料科学与工艺,2010(1):31-37. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%