为了探索不同外加电场及电极对钢液无污染脱氧的影响，基于电化学反应机理设计制作了适用于工业试验的外加电场钢液净化精炼装置，并开展了相应的数值模拟及工业试验研究。研究表明，在熔渣与钢液间施加外加电场，能有效进行电化学脱氧，最快脱氧速率可达0.00186%/min。任何增大氧离子传质系数和增大渣金反应面积的方法都可增大渣金间氧离子电流，提高脱氧反应速率。此方法是一种全新的绿色、环保洁净钢精炼工艺，具有十分广阔的应用前景。
In order to explore the influence of various applied electric fields and electrodes on the unpolluted deoxidiza-tion of molten steel,a new deoxidization system for commercial experiment and numerical simulation has been de-signed and fabricated based on the mechanism of electrochemical reaction. And the unpolluted deoxidization technique has been studied when a DC field was applied between the metal and slag. The results show that electrochemical deoxidi-zation can be carried out effectively with the application of electric field at the interface between metal and slag. The maximum deoxidization rate could reach 0.001 86%/min. Both increasing the mass transfer coefficient of oxygen ions and the reaction area of the metal and the slag could increase the oxygen ion current between the steel and slag,so the de-oxidization rate could be improved. This technology is new kind of green and environmental steel refining process, which has broad application prospects.
参考文献
| [1] | 赵东伟;李海波;高攀;杨健;郝丽霞.非钙处理铝脱氧车轮钢夹杂物形成及变形行为[J].钢铁,2016(1):25-32. |
| [2] | 马焕珣;王新华;黄福祥;季晨曦;潘宏伟.脱氧工艺对低碳铝镇静钢洁净度的影响[J].钢铁,2016(1):19-24. |
| [3] | 高运明;姜英;张华;郭兴敏;周国治.可控氧流冶金[J].武汉科技大学学报（自然科学版）,2007(5):449-453. |
| [4] | 高运明;郭兴敏;周国治.熔渣中氧传递机理的研究[J].钢铁研究学报,2004(4):1-6. |
| [5] | 鲁雄刚;梁小伟;袁威;孙铭山;丁伟中;周国治.渣金间外加电场无污染脱氧方法的研究[J].金属学报,2005(2):113-117. |
| [6] | 贾吉祥;廖相巍;赵刚;曹东;郭庆涛;朱晓雷.外加电场钢液无污染脱氧新方法[J].炼钢,2012(4):47-50. |
| [7] | 郭庆涛;贾吉祥;廖相巍;李广帮;曹东;李德刚.外加直流电场无污染脱氧模拟研究[J].鞍钢技术,2014(2):24-28. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%