步进梁连续式加热炉水印会导致中厚板轧制钢板厚度的波动。针对厚板加热炉的结构形式和厚板轧机控制模型的设定特点，研究出了一种可以针对加热炉水印位置进行轧制设定的控制方法。使用此方法可以对加热炉水印位置的轧制力进行单独设定，从而减轻甚至消除加热炉水印对厚板厚度的影响。在宝钢5m厚板轧机现场应用后，厚板厚度精度得到了明显改善。
The skid of walking beam slab reheating furnace can cause fluctuation on the final plate thickness during plate rolling. Based on analysis on both the structure of walking beam slab reheating furnace and controlling method of plate mill,a controlling method based on setting up on the skid position of slab was established. By using this controlling method,the fluctuation of plate thickness caused by reheating slab skid can be alleviated. After the application of this method,the thickness accuracy of plate produced by Baosteel 5 m plate mill was improved.
参考文献
| [1] | 戴平.提高热连轧厚度控制精度的实践与思考[C].2006年全国轧钢生产技术会议文集,2006:163-167. |
| [2] | 马东 .带钢热连轧AGC自动厚度控制的应用与研究[D].东北大学,2003. |
| [3] | Jong Gyu KIM;Kang Y.HUH.Prediction of Transient Slab Temperature Distribution ill the Re-heating Furnace of a Walking-beam Type for Rolling of Steel Slabs[J].ISIJ International,200011(11):1115-1123. |
| [4] | 朱伟素;陈海耿;肖楠;胡文超;潘小兵.步进梁式加热炉内钢坯和垫块数学模型[J].中国冶金,2007(4):38-41. |
| [5] | 刘向军;赵燕;潘小兵.步进式加热炉内钢坯加热过程的模拟研究[J].钢铁,2005(7):76-79. |
| [6] | 余汉林;刘广林.热轧带钢加热炉节能技术改造[J].钢铁,2001(1):60-61,59. |
| [7] | 刘铁男;黄作为;朱越.大型步进梁式加热炉汽化冷却装置[J].钢铁,2002(3):55-58. |
| [8] | 陈友文;柴天佑.工业加热炉温度设定的研究与应用[J].钢铁研究学报,2010(9):53-57. |
| [9] | 钟华春;李建华;张南风.模糊神经网络在加热炉温度控制中的应用[J].中国冶金,2014(3):18-20,33. |
| [10] | 闫振武.富氧燃烧在太钢加热炉的节能应用[J].钢铁,2015(2):85-89. |
| [11] | 韩仁志;谢安国;李先春;刘坤;张宇.热轧中间坯水印与成品精度关系分析[J].冶金能源,2006(3):30-31. |
| [12] | 黄涛;曹建国;张杰.带钢热连轧机KFF-AGC系统的研究与应用[J].武汉科技大学学报（自然科学版）,2009(1):41-44. |
| [13] | 梁辉;童朝南.基于轧制力信号多分辨分析的AGC系统[J].控制工程,2012(1):60-64. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%