针对特厚板连铸工艺的特点，分析了传统的中厚板连铸保护渣与特厚板连铸保护渣的作用特征差异。根据不同钢种在结晶器内的凝固特性，对新钢特厚板连铸保护渣进行了系列规划，分为高碳钢连铸保护渣、包晶钢连铸保护渣、中碳低合金钢连铸保护渣3大类。在此基础上，提出了保护渣熔化温度、黏度、转折温度、结晶比例的控制范围。生产实践表明，设计的保护渣浇铸过程结晶器内状况良好，渣面无结团、结块现象，液渣层厚度合适，保护渣消耗量正常，铸坯表面质量优良，连铸生产工艺顺行。
The characteristic differences between traditional mold fluxes for medium or thick slabs continuous casting and ultra-thick slabs continuous casting were analyzed based on the technological characteristics of ultra-thick slabs cast-ing. Then,the systematization of mold fluxes was conducted after the discussion of solidification features of for different grades,and three mold flux groups were proposed:high carbon steels,peritectic steels and micro alloying steels with me-dium carbon content. Based on the classification,the control ranges of melting temperature、viscosity、break temperature and crystallization ratio of mold fluxes were put forward. Commercial production data reveals that with proposed mold fluxes,smooth and stable casting can be obtained and no sintering is observed. The thickness of liquid slag layer and con-sumption are suitable. The surface quality of slabs is perfect and the continuous casting process is smooth.
参考文献
| [1] | 毛敬华;王水根;占贤辉.机型与防止特厚板坯表面裂纹的关系[J].连铸,2014(2):39-41. |
| [2] | 梁旭;周清跃;张银花;李闯.钢轨中大尺寸外来夹杂物分析[J].钢铁,2015(5):54-58. |
| [3] | 刘春秀;杜辰伟;兰鹏;张家泉.连铸保护渣与氧化铝的交互作用研究现状[J].中国冶金,2015(9):15-21. |
| [4] | 曹磊.包晶钢连铸坯表面纵裂与保护渣性能选择[J].钢铁,2015(2):38-42. |
| [5] | 李向奎;张丙龙;陈玉鑫;景财良.冷轧板表面夹杂缺陷成因及控制[J].中国冶金,2015(12):54-58. |
| [6] | 杨军;盛建华;陆力军;顾学红.马氏体不锈钢板坯连铸保护渣研制与应用[J].钢铁,2012(2):26-29. |
| [7] | 熊伟;彭其春;范丹萍;于学森;邱雷;杨进玲.低碳铝镇静钢连铸头坯夹杂物[J].中国冶金,2014(5):14-17. |
| [8] | 屈天鹏;韩志伟;冯科;赵和明;江小敏;阮细保.420mm特厚板坯连铸机生产实践[J].连铸,2012(4):23-26. |
| [9] | 王谦;何生平;李玉刚;朱礼龙;吴婷;陈卓.中国连铸保护渣技术现状及发展需求[J].连铸,2014(5):1-8. |
| [10] | K.C. Mills;A.B. Fox;Z. Li.Performance and properties of moulds fluxes[J].Ironmaking & Steelmaking: Products and applications,20051(1):26-34. |
| [11] | Jianfei XU;Shengping HE;Xueping JIANG.Analysis of Crack Susceptibility of Regular Carbon Steel Slabs Using Volume-Based Shrinkage Index[J].ISIJ International,201310(10):1812-1817. |
| [12] | 孙彦辉;赵长亮;蔡开科;杨素波;陈永;李桂军;顾武安.连铸板坯表层网状裂纹的成因研究[J].中国冶金,2008(4):15-20. |
| [13] | 曾建华,李桂军,杨素波,赵克文,王谦,李玉刚.高碳钢连铸保护渣润滑行为的数学模拟[C].第四届发展中国家连铸国际会议论文集,2008:689-692. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%