对冷轧无取向硅钢表面白线缺陷的特征和分布进行了描述,通过扫描电镜(SEM)分析、铸坯机清试验、连铸坯表面清洗检查、铸坯表面缺陷跟踪试验、塞棒吹气试验等,研究了产生白线缺陷的原因,并提出了此类缺陷的控制措施.结果表明:白线缺陷与连铸坯表面夹渣有关,缺陷的产生是与结晶器液面活跃程度及保护渣熔化状态有关.适当增大连铸塞棒吹氩量、增加拉速及优化保护渣物性参数,白线缺陷发生率由原来88%降至8%.
A kind of white sliver defect appeared on the cold-rolled sheet surface of non-oriented electrical steel was sys-tematically investigated in this paper,by performing the scanning electron microscopy (SEM) observation,slab scarfing examination,slab surface pickling treatment and the stopper blowing-argon experiment. The results show that the white sliver defect is originated from mold slag entrapment,which is related to the activation degree of the molten steel flow and the melting status of the powder. By appropriately increasing the blowing argon flow rate of the stopper,increasing the casting speed and optimizing the physical properties of the mold powder,the occurrence of white sliver defect rate on the cold-rolled sheet surface is reduced from 88%to 8%.
参考文献
| [1] | 黄璞,毛炯辉,陈卓,杨贤诚.我国冷轧无取向电工钢生产与技术水平的研究[C].第七届中国钢铁年会论文集,2009:3073-3086. |
| [2] | 王畅;于洋;徐海卫;王林;刘珂;陈瑾;李飞.连退板表面白线缺陷成因和控制措施[J].轧钢,2014(5):55-58. |
| [3] | 彭其春;赵金涛;田俊;陈永金;张学辉;彭胜堂.武钢冷轧板表面"黑线"缺陷分析[J].中国冶金,2010(1):21-25. |
| [4] | 齐海峰;唐广波;王晓春;李激光.无取向电工钢线状表面缺陷分析[J].钢铁钒钛,2012(4):96-100. |
| [5] | 彭其春;田俊;尹会芳;张学辉;彭胜堂;徐静波.冷轧板表面线状缺陷成因分析与探讨[J].武汉科技大学学报（自然科学版）,2009(1):15-19. |
| [6] | 孙彬;曹光明;贾涛;邹颖;刘振宇;王国栋.热轧高强钢氧化铁皮演变规律的研究[J].钢铁,2010(11):53-56,81. |
| [7] | Qiaotong Lu;Rongguang Yang;Xinhua Wang;Jiongming Zhang;Wanjun Wang.Water modeling of mold powder entrapment in slab continuous casting mold[J].北京科技大学学报（英文版）,2007(05):399-404. |
| [8] | 孙云虎;罗传清;王延峰;张华.低碳钢板坯表面夹渣的研究与控制[J].炼钢,2013(5):30-33. |
| [9] | 曾亚南;孙彦辉;艾西;马志飞;刘瑞宁;刘泳.结晶器保护渣对300 mm×360 mm低碳钢连铸坯表面质量的影响和成分优化[J].特殊钢,2014(4):24-27. |
| [10] | 张立峰;李燕龙;任英.钢中非金属夹杂物的相关基础研究（Ⅰ）--非稳态浇铸中的大颗粒夹杂物及夹杂物的形核、长大、运动、去除和捕捉[J].钢铁,2013(11):1-10. |
| [11] | 黄琦;熊霄;邓小旋;王新华;王万军;姜敏.凝固坯壳对高拉速板坯连铸结晶器钢水流动特征的影响[J].钢铁,2015(1):37-42. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%