倒角结晶器是控制板坯角部横向裂纹的有效方法之一，但角部纵向裂纹是倒角连铸坯易发的缺陷，这成为了倒角结晶器大规模应用的最大障碍。通过研究倒角结晶器生产工艺参数、设备精度以及喷嘴堵塞等因素对倒角连铸坯角部纵向裂纹的影响，确定了角部纵向裂纹发生的机制。研究表明，倒角结晶器窄面锥度不合理、0段和1段连接偏差以及喷嘴堵塞等是角部纵向裂纹产生的主要原因。通过采取有效措施，可以将倒角连铸坯角部纵向裂纹发生率降低到0.6%以下，使得倒角结晶器实现大规模的工业应用。
Chamfering mold is one of the effective methods for controlling the transverse corner cracking of slab. Howev-er the longitudinal corner cracking will occur in slab with chamfering mold,which is the most critical hinder for wide us-age of chamfering mold. The effects on longitudinal corner cracking of chamfered slab of process parameters and equip-ment accuracy as well as spray nozzle blocking are analyzed. The formation mechanism of longitudinal corner cracking has been found. Research shows that,the main causes of longitudinal corner cracking are the inconsequence taper of nar-row face,the deviation of 0 and 1 section connection and spray nozzle clogging. Through effective measures,chamfering mold can be extensively applied to industry manufacture as the percentage of occurrence for longitudinal corner cracking of CC slab is reduced below 0.6%.
参考文献
| [1] | 刘洋,王文军,朱志远,王凤琴,关春阳,韦耀环.利用倒角结晶器消除连铸板坯的角横裂纹缺陷[J].钢铁,2012(04):47-50. |
| [2] | 王文军,李本海,朱志远,刘洋,王玉龙,关春阳.板坯连铸倒角结晶器的开发与应用[J].钢铁研究学报,2012(09):21-26. |
| [3] | 张慧,吴夜明,王明林,陶红标,王一成,干勇.微合金化钢板坯角部横裂纹控制技术开发及应用[C].第十八届(2014年)全国炼钢学术会议论文集,2014:1-11. |
| [4] | 曹建新,陶红标,张慧,周明伟,张亮洲,彭明耀.倒角结晶器在涟钢板坯连铸生产中的应用[J].钢铁,2013(11):43-47. |
| [5] | 赵艳玲,王淑满,王洪兴,常立山.X80管线钢的生产实践[J].中国冶金,2014(8):17-21. |
| [6] | 冯科,韩志伟,王勇,毛敬华.板坯连铸结晶器窄面理论锥度的仿真预测[J].钢铁技术,2008(02):15-16,35. |
| [7] | LIU Yang,刘洋,WANG Wen-jun,王文军,ZHU zhi-yuan,朱志远,GUAN Chun-yang,关春阳,WEI Yao-huan,韦耀环,WANG Yu-long,王玉龙.连铸板坯倒角结晶器技术在首秦公司的成功开发与应用[C].2012年全国炼钢-连铸生产技术会论文集,2012:754-759. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%