以首钢京唐实际生产过程中倒角结晶器的铜板尺寸、水道布置、铜板实测温度、宽窄面水量和进出水温差为基础，运用商业软件ANSYS模拟了实际生产过程中倒角结晶器铜板温度分布。计算结果表明：距弯月面0～300 mm，倒角结晶器窄面横向温度分布呈W型，和直角结晶器倒U型温度分布有很大差别；距弯月面300～800 mm，角部温度迅速降低，温度分布呈倒U型，和直角结晶器温度分布基本一致；此外，倒角结晶器倒角面的温度梯度较大，倒角面上坯壳与铜板之间的换热热流波动较大，这说明倒角坯的缺陷主要出现在倒角面，这与实际是相符合的。
Based on the dimension of chamfered mold,waterway arrangement,measured copper temperature,cooling water volume and temperature difference between inlet and outlet water in actual production process of Beijing Steel Plant,the commercial software ANSYS was used to simulate the chamfered copper mold temperature distribution in actual production. The results show that from the meniscus 0-300 mm,the lateral temperature distribution on narrow-surface coo-per was W type,which is different from the right-angle mold inverted U type temperature distribution. From the meniscus 300-800 mm,the corner temperature decreases quickly,thus the temperature distribution was inverted U type,which is consistent with right-angle mold temperature distribution. In addition,the temperature gradient is relatively large in cham-fered slope,and the heat-flux fluctuations between the solidified shell and copper is relatively large,which verifies the cracks occurred mainly in the chamfered slope,be consistent with the fact.
参考文献
| [1] | 曹建新,陶红标,张慧,周明伟,张亮洲,彭明耀.倒角结晶器在涟钢板坯连铸生产中的应用[J].钢铁,2013(11):43-47. |
| [2] | 刘洋,王文军,朱志远,王凤琴,关春阳,韦耀环.利用倒角结晶器消除连铸板坯的角横裂纹缺陷[J].钢铁,2012(04):47-50. |
| [3] | 刘增勋,张海辉,刘建敏,安振亮.方坯结晶器内气隙分布的数值分析[J].中国冶金,2012(05):13-17. |
| [4] | 荆德君,蔡开科.连铸结晶器内铸坯温度场和应力场耦合过程数值模拟[J].北京科技大学学报,2000(05):417-421. |
| [5] | 王晓晨,孙齐松,邸全康,丁宁,程四华,周剑波.薄腹板近终形异形坯连铸温度场数值模拟[J].钢铁,2013(12):36-40. |
| [6] | 冯科,徐楚韶,陈登福,陈光碧.板坯连铸结晶器铜板温度场的数值仿真[J].特殊钢,2005(01):12-15. |
| [7] | 杨晓江,张慧,胡鹏,杨杰,钟周,郝占全.非均匀冷却型结晶器铜板的传热特性[J].钢铁研究学报,2014(7):23-27. |
| [8] | 陈阳,钟光,姚军,宁曙光,李桢,谢长川.双流板坯结晶器锥度动态保持技术的开发与应用[J].钢铁,2014(10):34-39. |
| [9] | 陶红标,吕晓军,席常锁,张慧,吴夜明,干勇.薄板坯连铸结晶器锥度设计技术研究及应用[J].钢铁,2012(01):28-33. |
| [10] | 丁毅,张慧,陶红标,张宗宁,陈远清,刘爱强.马钢CSP工艺漏斗型结晶器铜板温度检测及传热分析[J].钢铁,2009(12):32-37. |
| [11] | 赵亮 .超宽板坯包晶钢连铸结晶器内温度场与应力场数值模拟[D].沈阳:东北大学,2008. |
| [12] | 兰岳光,邹宗树,王晓鸣.结晶器角部气隙厚度对方坯温度场影响的数值模拟[J].过程工程学报,2003(06):518-522. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%