采用热力学计算软件对LF2合金中的析出相进行计算，采用扫描电子显微镜、透射电子显微镜、微细相分析以及拉伸试验，对不同钛质量分数的LF2合金的微观组织和力学性能进行了研究，结果表明：LF2合金中γ′相以近球形在晶内弥散析出，尺寸约为20 nm，Laves相在晶界以纤维状和块状析出；随钛质量分数增加，γ′相数量增加，钛质量分数增加了0.92%，γ′相的质量分数是原来的1.35倍；Laves相数量增多，由纤维状变为短棒状。随钛质量分数增加，LF2强度增加，γ′相强化效果相对减弱，但γ′相仍然是最主要的强化相。
Equilibrium precipitation phases of LF2 alloys were studied by using a thermodynamic Thermo-Calc soft-ware,microstructure and mechanical properties of LF2 alloys bearing different Ti content were studied by using scanning electron microscopy,transmission electron microscopy,subtle phase analysis and tensile test. The results show that γ′phase is diffusely distributed in transgranular substantially spherical which size is about 20 nm. Laves phase precipitated with fibrous and block in the grain boundary. With the increase of Ti content of,the content ofγ′phase increased,Ti con-tent has increased 0.92 percent,the quality percentage of Laves phase is 1.35 times of the original,the content of Laves phase increased,transforming fibrous into short clavate shape. With the increase of Ti content,the strength of LF2 alloys increases,strengthening effect ofγ′phase is relatively weak,butγ′phase is still the main strengthening phase.
参考文献
| [1] | 梁小威.对中国加入WTO后的国内特殊钢供需预测探讨[J].武汉科技大学学报(社会科学版),2000(03):17-20. |
| [2] | 董瀚;张永权;李桂芬.汽车用钢的现状与未来[J].世界汽车,1997(4):4. |
| [3] | 余式昌,吴申庆,宫友军,宫元生,练明生.6Cr21Mn10MoVNbN气阀钢晶粒长大及其动力学研究[J].钢铁,2006(06):71-76. |
| [4] | 韩凤奎,燕平,赵京晨,张龙飞,曾强.长期时效对DD407单晶高温合金组织和中温性能的影响[J].钢铁研究学报,2011(09):55-58. |
| [5] | 李卫,唐正友,王玫,丁桦,杨平.高锰奥氏体TRIP/TWIP钢的组织和力学性能[J].钢铁,2007(01):71-75. |
| [6] | 程世长;林肇杰 .中国内燃机气阀钢发展趋势[J].特殊钢,1996,12(5):5. |
| [7] | 程世长,刘正东,杨钢,林肇杰.中国内燃机气阀钢的现状和建议[J].钢铁研究学报,2005(03):1-4. |
| [8] | 牛旭斐,程世长,朱云,李玲霞,谌康.700℃长时时效对LF2合金组织和高温拉伸性能的影响[J].机械工程材料,2012(03):39-42,100. |
| [9] | 谌康,程世长,张军战,包汉生,牛旭斐.大块含铌MC碳化物对LF2合金高温性能的影响[J].机械工程材料,2012(03):18-21,25. |
| [10] | 阳东海 .国内阀门钢的生产研究和发展[J].特殊钢,1996,17(3):16. |
| [11] | 薛润东,谢建新,李杏娥.钛含量对热轧带钢奥氏体晶粒长大与析出特性的影响[J].钢铁研究学报,2013(10):31-35. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%