利用光学显微镜、扫描电子显微镜等分析了闪光对焊焊接380CL钢轮辋焊缝开裂的原因。结果表明：该轮辋焊缝的开裂为脆性开裂，焊缝区晶粒异常长大及焊后冷速较快而产生的粗大魏氏组织是其失效的根本原因；通过优化闪光对焊工艺，降低焊接时焊缝中心高温停留时间以有效控制焊缝奥氏体晶粒尺寸，可以保证焊缝良好的强韧性、避免焊缝开裂。
The weld cracking reason of 380CL steel rim welded by flash butt welding was analyzed by using optical microscope,scanning electron microscope and so on.The results show that the weld cracking of the rim was brittle cracking.The coarse widmanst?tten structure,which was produced due to the abnormal growth of grains in weld seam and the rapid cooling rate after welding,was the main reason for the cracking failure.By optimizing the flash butt welding process,shortening high-temperature residence time in the weld center to effectively control the weld austenite grain size and ensuring a good strength and toughness property of the weld would prevent the weld cracking.
参考文献
| [1] | 赵红利;李发云;罗成;吴放.汽车滚型轮辋闪光对焊开裂分析[J].焊接技术,2009(3):56-58. |
| [2] | 熊春英;张亚舫;罗学泉;陈剑;唐新民.国产化材料车轮钢圈焊接工艺的确定[J].机械工程材料,2014(12):50-53,86. |
| [3] | 辜纯民;邓卫华;杨成刚;柯黎明;黄春平.搅拌摩擦焊工艺参数对LY12铝合金接头组织和力学性能的影响[J].机械工程材料,2008(6):22-24. |
| [4] | 张桂芹;董建君;王燕;赵文成.380CL车轮钢闪光对接焊组织与性能[J].热加工工艺,2012(15):141-142. |
| [5] | 黄华刚;王克争;何方殿;吴建新;刘文铎.闪光对焊接头金相组织、性能和工艺关系的研究[J].焊接,2000(11):11-13. |
| [6] | 张根元;陈洪莲;徐迈里;吴建建.45钢交流闪光对焊焊接热影响区晶粒长大的数值模拟[J].机械工程材料,2008(7):75-78,86. |
| [7] | 李敏;宋振官.380CL钢制轮辋焊缝开裂分析[J].宽厚板,2013(4):28-30. |
| [8] | 吴丰顺;张贵锋;王士元;史耀武.直流电阻对焊过程的有限元分析[J].机械工程学报,1998(6):90-96. |
| [9] | 张德芬;李曾珍;罗红松;王同举.不预热焊接工艺焊接X70管线钢接头的组织与性能[J].机械工程材料,2014(12):37-41,96. |
| [10] | 李继红;杨亮;张兴璇;张敏.超低碳微合金管线钢焊接接头的组织与冲击性能[J].机械工程材料,2014(6):75-78. |
| [11] | 王维斌;史耀武;雷永平;田志凌.400 Mpa超细晶粒钢直流电阻闪光对焊接头组织的数值模拟[J].机械工程学报,2005(1):77-81. |
| [12] | 赵雷;乔汉文;梁军;钟群鹏;徐连勇;肖德铭.焊接参数对T92/S30432异种钢焊接接头室温力学性能的影响[J].机械工程材料,2015(1):32-38. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%