在轮轨模拟试验机上模拟了列车车轮在高速(350 km.h－1)和低速(120 km.h－1)工况下的运行过程，对比分析了两种工况下车轮的损伤行为.结果表明：两种工况下车轮试样均出现了非均匀磨损，表面磨痕沿车轮滚动方向交替出现了光滑区域和粗糙区域；低速工况下车轮试样的磨损量明显大于高速工况下的，其粗糙区域和光滑区域的损伤差异性较大，而高速工况下两个区域的损伤差异性较小.
The running processes of railway wheel under high speed (350 km.h-1 )and low speed (120 km. h-1 )conditions were simulated on the wheel/rail simulation facility,and the the damage behaviors of the wheel under the two conditions were compared and analyzed.The results show that the irregular wear appeared on both wheel specimens under the two conditions,namely the smooth and rough region appeared alternately along the rolling direction of wheel on the surface wear mark.The mass loss of wheel specimen under low speed condition was significantly greater than that under high speed condition and the damage difference was relatively large between smooth and rough areas.However,under the high speed condition,the difference was relatively small.
参考文献
| [1] | N. Lingamanaik, S.;Chen, B.K..Prediction of residual stresses in low carbon bainitic-martensitic railway wheels using heat transfer coefficients derived from quenching experiments[J].Computational Materials Science,2013:153-160. |
| [2] | Adam Bevan;Paul Molyneux-Berry;Bridget Eickhoff;Mark Burstow.Development and validation of a wheel wear and rolling contact fatigue damage model[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20131/2(1/2):100-111. |
| [3] | 马跃;潘涛;江波;崔银会;苏航;彭云.S含量对高速车轮钢断裂韧性影响的研究[J].金属学报,2011(8):978-983. |
| [4] | 曾东方;鲁连涛;张远彬;张继旺;朱旻昊;金学松.高速轮轨材料匹配的滚动接触磨损性能[J].机械工程学报,2013(13):183-189. |
| [5] | 刘吉华;周桂源;刘启跃.四种成分车轮钢的耐磨性及疲劳特性[J].机械工程材料,2013(5):80-84. |
| [6] | 申鹏 .轮轨黏着特性试验研究[D].西南交通大学,2012. |
| [7] | 钟雯;董霖;王宇;朱维兵;刘启跃.高速与重载铁路的疲劳磨损对比研究[J].摩擦学学报,2012(1):96-101. |
| [8] | Q. Y. Liu;B. Zhang;Z. R. Zhou.An experimental study of rail corrugation[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20037/12(7/12):1121-1126. |
| [9] | D. Zapata;J. Jaramillo;A. Toro.Rolling contact and adhesive wear of bainitic and pearlitic steels in low load regime[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20111/2(1/2):393-399. |
| [10] | K. Cvetkovski;J. Ahlstrom.Characterisation of plastic deformation and thermal softening of the surface layer of railway passenger wheel treads[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20131/2(1/2):200-204. |
| [11] | F. Wetscher;R. Stock;R. Pippan.Changes in the mechanical properties of a pearlitic steel due to large shear deformation[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20070(0):237-243. |
| [12] | John E. Garnham;Claire L. Davis.The role of deformed rail microstructure on rolling contact fatigue initiation[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20089/10(9/10):1363-1372. |
| [13] | Anders Ekberg;Bengt Akesson;Elena Kabo.Wheel/rail rolling contact fatigue - Probe, predict, prevent[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20141/2(1/2):2-12. |
| [14] | 张永利 .轮轨垂向高频振动的研究[D].大连交通大学,2005. |
| [15] | Abdel-Karim M.;Ohno N..Kinematic hardening model suitable for ratchetting with steady-state[J].International Journal of Plasticity,20003-4(3-4):225-240. |
| [16] | Anders Ekberg;Elena Kabo.Fatigue of railway wheels and rails under rolling contact and thermal loading - an overview[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20057/8(7/8):1288-1300. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%