对相同成分的550 MPa级高强韧船板钢进行了常规轧制和控制轧制，对比了轧后试验钢的显微组织和力学性能.结果表明：两种工艺轧制试验钢的组织均为铁素体＋M/A 岛；控制轧制试验钢的晶粒更细小，铁素体含量更高；两种工艺轧制试验钢的强度和伸长率相差不大，但控制轧制试验钢在－40℃的低温冲击功更高，为常规轧制试验钢的2．4倍.
Normal rolling and controlled rolling processes were carried out on 550 MPa rank high strength-toughness hull plate steel with same chemical composition,and microstructures and mechanical properties of the steel after rolling were compared.The results show that microstructures of the steel after rolling with two kinds of processes were ferrite and M/A island,the grain size of the steel with controlled rolling was a little smaller,and the content of ferrite was higher.Strength and elongation of the steel after rolling with two kinds of processes had little difference,but the steel with controlled rolling had higher low temperature impact energy at -40 ℃,which was 2.4 times of impact energy of the steel with normal rolling.
参考文献
| [1] | 杨升山;李丽;蔡建伟;苏航;王青峰.正火冷速对10MnNiCr船体钢M-A岛和韧性的影响[J].钢铁,2010(9):72-76. |
| [2] | 杨景红;刘刚.回火工艺对连轧10MnNiCr钢板组织性能的影响[J].材料开发与应用,2012(5):8-11. |
| [3] | 张永权;张荣久;苏航;李丽.粒状贝氏体对10MnNiCr微合金钢力学性能的影响[J].钢铁,2003(11):45-47,39. |
| [4] | 何立新;陈连生;王刚;顾克井.轧制工艺对J55石油套管用带钢带状组织的影响[J].轧钢,2012(6):18-23. |
| [5] | 余宏伟;王孝东;洪君;熊涛;梁宝珠.轧制工艺对高强度建筑钢板组织和屈强比的影响[J].金属材料与冶金工程,2012(1):11-14. |
| [6] | 尹桂全;尹云洋;王世俊;田海林;程坚平;程晓舫.微合金V-N钢轧制工艺与显微组织[J].金属热处理,2005(11):43-46. |
| [7] | 范建文;谢瑞萍;张维旭;代晓莉;金永春;王祖滨.普通C-Mn钢超细晶中厚板的带状组织[J].钢铁,2004(8):100-104. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%