将碳纤维/环氧树脂复合材料在温度为71℃、相对湿度为85％的环境下吸湿至平衡后研究了它的吸湿行为,然后分别在室温和71,93,116,132℃下进行了弯曲性能、纵横剪切性能、动态力学性能试验,研究了该复合材料湿热老化后的力学性能.结果表明：碳纤维/环氧树脂复合材料的吸湿率较低,其饱和吸湿率仅为0．91％左右；湿热老化后,复合材料的弯曲强度保持率在50％以上,弯曲模量保持率在80％以上,纵 横 剪 切 强 度 保 持 率 在55％以上,其玻璃化转变温度为195℃,极限耐热温度可达到132℃；该碳纤维/环氧树脂复合材料具有良好的耐湿热老化能力.
A carbon fiber/epoxy resin composite moisture absorbed to balance at 71 ℃ and relative humidity 85%,and then its moisture absorption behavior was studied,and some tests was carried out,such as bending properties,in-plane shear properties and dynamic mechanical properties testing,the mechanical properties of the composite after hygrothermal aging were studied.The results show that the moisture absorption of the composite was low and was just about 0.91%.After hygrothermal aging,bending strength retention rate of the composite was more than 50%,bending modulus retention rate was more than 80% and in-plane shear retention rate was more than 55%.Glass transition temperature and extreme temperature of the wet composite was 1 95 ℃ and 132 ℃, respectively.The carbon fiber/epoxy composite has good hygrothermal aging resistance.
参考文献
| [1] | 吕新颖;江龙;闫亮;王荣国;刘文博.碳纤维复合材料湿热性能研究进展[J].玻璃钢/复合材料,2009(3):76-80. |
| [2] | Bahrami A;Nosier A.Interlaminar hygrothermal stresses in laminated plates[J].International Journal of Solids and Structures,200725/26(25/26):8119-8142. |
| [3] | 封彤波;肇研;罗云烽;张佐光.循环湿热环境下碳纤维复合材料的界面性能[J].北京航空航天大学学报,2010(12):1427-1431. |
| [4] | 吕小军;张琦;马兆庆;许俊华;肖文萍.湿热老化对碳纤维/环氧树脂基复合材料力学性能影响研究[J].材料工程,2005(11):50-53,57. |
| [5] | 彭雷;张建宇;鲍蕊;费斌军.湿热、紫外环境对T300/QY8911复合材料孔板静力性能的影响[J].复合材料学报,2009(3):18-23. |
| [6] | Ray BC.Temperature effect during humid ageing on interfaces of glass and carbon fibers reinforced epoxy composites[J].Journal of Colloid and Interface Science,20061(1):111-117. |
| [7] | 李敏;张宝艳.5428/T700复合材料的耐湿热性能[J].纤维复合材料,2006(1):3-4,8. |
| [8] | 詹茂盛;李小换;许文;刘宇.热氧、湿热和热水老化对T300/BHEP复合材料玻璃化转变温度的影响[J].宇航材料工艺,2011(3):56-60. |
| [9] | 余治国;杨胜春;宋笔锋.T700和T300碳纤维增强环氧树脂基复合材料耐湿热老化性能的对比[J].机械工程材料,2009(6):48-51. |
| [10] | 陈涛;何宇廷;邵青;冯宇;张腾.湿热环境对纤维增强树脂基复合材料加筋板剪切性能的影响[J].机械工程材料,2014(4):59-62. |
| [11] | Bhavesh G.Kumar;Raman P.Singh;Toshio Nakamura.Degradation of Carbon Fiber-reinforced Epoxy Composites by Ultraviolet Radiation and Condensation[J].Journal of Composite Materials,200224(24):2713-2733. |
| [12] | 李晓骏;陈新文.复合材料加速老化条件下的力学性能研究[J].航空材料学报,2003(z1):286-286. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%