碳钢表面自组装邻氧乙酸苯甲醛缩间氨基苯甲酸二钾席夫碱(K2L2)缓蚀膜.采用极化曲线、电化学阻抗谱和扫描电镜研究了自组装缓蚀膜在模拟实际工作环境中对碳钢的缓蚀性能.结果表明:矿化度、温度、pH、流动状态和H2S含量对自组装缓蚀膜在CO2饱和油田水中的缓蚀性能具有一定的影响,但仍有较高的缓蚀率,当油田水中H2S质量分数为200 mg/L时,缓蚀率达到80.0％.
参考文献
| [1] | H. Luo;Y. C. Guan;K. N. Han.Corrosion inhibition of a mild steel by aniline and alkylamines in acidic solutions[J].Corrosion: The Journal of Science and Engineering,19989(9):721-731. |
| [2] | M. Behpour;S.M. Ghoreishi;N. Mohammadi;N. Soltani;M. Salavati-Niasari.Investigation of some Schiff base compounds containing disulfide bond as HCl corrosion inhibitors for mild steel[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,201012(12):4046-4057. |
| [3] | 李春福 .油气开发过程中的CO<,2>腐蚀机理及防护技术研究[D].西南石油学院,2005. |
| [4] | 任呈强 .N80油管钢在含CO<,2>/H<,2>S高温高压两相介质中的电化学腐蚀行为及缓蚀机理研究[D].西北工业大学,2003. |
| [5] | Govindaraju, KM;Gopi, D;Kavitha, L.Inhibiting effects of 4-amino-antipyrine based schiff base derivatives on the corrosion of mild steel in hydrochloric acid[J].Journal of Applied Electrochemistry,200912(12):2345-2352. |
| [6] | 全贞兰;陈慎豪;华兰;雷圣宾;崔学桂.希夫碱在铜表面上的自组装膜的STM和XPS研究[J].科学通报,2001(19):1618-1621. |
| [7] | Ismail Abdelrhman Aiad;Nabel A. Negm.Some Schiff Base Surfactants as Steel-Corrosion Inhibitors[J].Journal of Surfactants and Detergents,20094(4):313-319. |
| [8] | 杨立红;李建平;石在虹;陈长风.两种油管材料在模拟油田水溶液中的CO_2腐蚀行为[J].腐蚀科学与防护技术,2010(2):131-135. |
| [9] | 李强 .Cr13钢在饱和CO2/H2S介质中的腐蚀与防护研究[D].北京化工大学,2011. |
| [10] | 徐群杰;周国定;陆柱.苯并三氮唑和5羧基苯并三氮唑对铜缓蚀作用的光电化学比较[J].中国有色金属学报,2001(5):925-929. |
| [11] | 陈长风 .油套管钢CO<,2>腐蚀电化学行为与腐蚀产物膜特性研究[D].西北工业大学,2002. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%