为解决多孔NiTi合金耐蚀性降低和Ni离子释放量增大而引起的使用安全性问题。本文采用微弧氧化技术对医用多孔NiTi合金进行表面改性处理，研究结果表明，微弧氧化处理并未改变多孔NiTi合金原有的孔隙结构和孔隙率，只在其外表面和孔隙内表面均形成了典型的微弧氧化多孔涂层。该涂层主要由氧化铝相组成，并含有少量的Ti和Ni元素，且外表面涂层的Ti和Ni含量要略低于孔隙内表面涂层。微弧氧化涂层提高了多孔NiTi合金的表面接触角，将原有的亲水表面转变成了疏水表面。经微弧处理后，多孔NiTi合金的耐蚀性较基体提高了1个数量级以上，Ni离子释放量也较基体降低了1个数量级以上。
In this paper, the biomedical porous NiTi alloys were modified by micro?arc oxidation method, and the effect of micro?arc oxidation treatment on the microstructure and corrosion resistance of the porous NiTi alloys were also studied. The results showed that the pore structure and the porosity of the porous NiTi alloy was not changed after micro?arc oxidation treatment. The typical micro?arc oxidation porous coating was formed both on the outside surface and inside surface of the porous NiTi alloy. This coating was mainly composed of alumina phase with a little Ti and Ni element, while the contents of Ti and Ni on the outside coating were lower than those of inside coating. The surface contact angle of the porous NiTi alloys were increased due to the micro?arc coating, which made the original hydrophilic surface transform into hydrophobic surface. Moreover, the corrosion resistance of coated porous NiTi alloys were enhanced by more than one order of magnitude compared to the uncoated porous NiTi alloy, and the release number of Ni+was decreased by more than one order of magnitude.
参考文献
| [1] | Bansiddhi,A;Sargeant,TD;Stupp,SI;Dunand,DC .Porous NiTi for bone implants: A review.[J].Acta Biomaterialia,2008(4):773-782. |
| [2] | 刘辉,憨勇.医用多孔金属的制备及其生物活化研究进展[J].中国材料进展,2012(05):40-56. |
| [3] | 张新平,张宇鹏.多孔NiTi形状记忆合金研究进展[J].材料研究学报,2007(06):561-569. |
| [4] | Jiang HC;Rong LJ .Effect of hydroxyapatite coating on nickel release of the porous NiTi shape memory alloy fabricated by SHS method[J].Surface & Coatings Technology,2006(3/4):1017-1021. |
| [5] | Yong-Hua Li;Guang-Bin Rao;Li-Jian Rong .Effect of pores on corrosion characteristics of porous NiTi alloy in simulated body fluid[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):356-359. |
| [6] | SUN X T;KANG Z X;ZHANG X P et al.A comparative study on the corrosion bebavior of porous and dense NiTi shape memory alloys in NaCl solution[J].Electrochimica Acta,2011,56:6389-6396. |
| [7] | Wu S;Liu X;Chan YL;Ho JP;Chung CY;Chu PK;Chu CL;Yeung KW;Lu WW;Cheung KM;Luk KD .Nickel release behavior, cytocompatibility, and superelasticity of oxidized porous single-phase NiTi.[J].Journal of biomedical materials research, Part A,2007(4):948-955. |
| [8] | J.P.Y. Ho;S.L. Wu;R.W.Y. Poon;C.Y. Chung;S.C. Tjong;P.K. Chu;K.W.K. Yeung;W.W. Lu;K.M.C. Cheung;K.D.K. Luk .Oxygen plasma treatment to restrain nickel out-diffusion from porous nickel titanium orthopedic materials[J].Surface & Coatings Technology,2007(9/11):4893-4896. |
| [9] | J.X. Zhang;R.F. Guan;X.P. Zhang .Synthesis and characterization of sol-gel hydroxyapatite coatings deposited on porous NiTi alloys[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2011(13):4643-4648. |
| [10] | LEMAIRE V;SICOTTE B;ALLARD S.Surface modification treatments to reduce Ni leaching from porous nitinol [z][A].Montreal,2007 |
| [11] | Y W Gu;B Y Tay;C S Lim .Nanocrystallite apatite formation and its growth kinetics on chemically treated porous NiTi[J].Nanotechnology,2006(9):2212-2218. |
| [12] | 李强,于景媛,孙旭东.多孔NiTi合金直流-脉冲阳极氧化表面改性研究[J].稀有金属材料与工程,2010(07):1270-1274. |
| [13] | 鲍路姿,徐吉林,罗军明,钟震晨,黄文亮,何军强.医用多孔NiTi合金的制备及表面改性研究进展[J].热加工工艺,2012(14):56-59,62. |
| [14] | A. L. Yerokhin;X. Nie;A. Leyland;A. Matthews;S. J. Dowey .Plasma electrolysis for surface engineering[J].Surface & Coatings Technology,1999(2/3):73-93. |
| [15] | J.L. Xu;F. Liu;F.P. Wang .The corrosion resistance behavior of Al_2O_3 coating prepared on NiTi alloy by micro-arc oxidation[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2009(1/2):276-280. |
| [16] | J.L Xu;F. Liu;F.P. Wang;D.Z. Yu;LC. Zhao .Microstructure and corrosion resistance behavior of ceramic coatings on biomedical NiTi alloy prepared by micro-arc oxidation[J].Applied Surface Science,2008(20):6642-6647. |
| [17] | J.L. Xu;F. Liu;F.P. Wang;L.C. Zhao .Alumina coating formed on medical NiTi alloy by micro-arc oxidation[J].Materials Letters,2008(25):4112-4114. |
| [18] | M. Sandhyarani;N. Rameshbabu;K. Venkateswarlu.Surface morphology, corrosion resistance and in vitro bioactivity of P containing ZrO_2 films formed on Zr by plasma electrolytic oxidation[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2013:324-332. |
| [19] | J. L. Xu;Z. C. Zhong;D. Z. Yu;F. Liu;J. M. Luo .Effect of micro-arc oxidation surface modification on the properties of the NiTi shape memory alloy[J].Journal of Materials Science. Materials in Medicine,2012(12):2839-2846. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%