为解决摩托车铝合金缸体压铸件存在的缺陷问题，利用AnyCasting铸造数值模拟分析软件，采用正交试验方法，并借助ImageJ软件统计铸件的孔洞面积（缩孔缩松或气孔），系统研究了压铸工艺参数：快压射速度、快压射切换点位置及模具温度对摩托车铝合金缸体孔洞面积的影响规律．研究表明，铸件内的孔洞总面积随着快压射速度的增加而增加，随着快压射切换点位置和模具预热温度的增加而减小．本实验条件下的最优工艺参数为：快压射速度2．0 m／s、快压射切换位置280 mm、模具温度240℃．采用该组参数，使铸件致密度增大，上、下端面孔洞所占面积分别减少21％和68％，铸件废品率从14％降低到5％．
In order to solve the defects problem of aluminum alloy cylinder body casting for motorcycle, the effects of fast shot velocity, fast shot set point and mold temperature on the porosity area ( shrinkage cavity, shrinkage porosity and air hole ) of aluminum alloy cylinder body casting for motorcycle were systematically investigated using orthogonal experiment method and theoretical simulation in which AnyCasting numerical simulation software and ImageJ statistics software were exploited. The results indicate that the total porosity area of the casing increases with the increasing of the fast shot velocity,while decreases with the rising of fast shot set point and mold temperature. The optimal parameters are: fast shot velocity-2. 0 m/s, fast shot set point-280 mm and mold temperature-240℃. Using this set of the optimal parameters, the casting density was increased , the percentages of porosity area on the top surface and bottom surface of the casting were decreased about 21% and 68% ,respectively, and the casting scrap rate was reduced from 14% to 5%.
参考文献
| [1] | 杨亚琴 .电机转子压力铸造工艺及参数优化研究[D].苏州大学,2009. |
| [2] | 汪之清.充氧压铸[J].特种铸造及有色合金,1996(3):38-41. |
| [3] | 吴先敬.铝合金轮毂的充氧压铸[J].有色金属加工,1998(2):6-9. |
| [4] | 孙林,苏勇,王东岭,刘伟,梁国萍.基于数值模拟的缸体压铸浇注系统位置选择[J].特种铸造及有色合金,2010(01):62-64. |
| [5] | Hong Yan;Wenwei Zhuang;Yong Hu;Qiansheng Zhang;Hong Jin .Numerical simulation of AZ91D alloy automobile plug in pressure die casting process[J].Journal of Materials Processing Technology,2007(0):349-353. |
| [6] | Guilherme Ourique Verran;Rui Patrick Konrad Mendes;Marco Aurelio Rossi .Influence of injection parameters on defects formation in die casting Al12Si1,3Cu alloy: Experimental results and numeric simulation[J].Journal of Materials Processing Technology,2006(1/3):190-195. |
| [7] | 张文,张绪平,朱洪睿,祁晓乾.YZ108气缸套压力铸造工艺参数优化[J].热加工工艺,2012(03):41-43. |
| [8] | 赵鑫 .高硅铝合金压铸孔隙率研究及工艺优化[D].上海交通大学,2009. |
| [9] | BAI Yue-long,MAO Wei-min,XU Jun,XU Hong,HOU Hua.Numerical simulation on rheo-diecasting mould filling of semi-solid key-shaped component[J].中国有色金属学会会刊（英文版）,2008(03):682-685. |
| [10] | ZHAO Hai-dong,BAI Yan-fei,OUYANG Xiao-xian,DONG Pu-yun.Simulation of mold filling and prediction of gas entrapment on practical high pressure die castings[J].中国有色金属学报（英文版）,2010(11):2064-2070. |
| [11] | 周君华,孙长波,尚伟,李波.ProCAST软件在熔模铸造工艺优化中的应用[J].材料科学与工艺,2013(05):109-112. |
| [12] | 华隆政.选择压力铸造高速压射切换点的经验和计算方法[J].特种铸造及有色和金,2000(1):64-65. |
| [13] | 于海朋,王峰,于宝义,宋鸿武,段华伟.工艺参数对压铸AM50组织和力学性能的影响[J].铸造,2004(08):645-648. |
| [14] | 孙林 .汽车铝合金发动机缸体压力铸造过程数值模拟[D].合肥工业大学,2010. |
| [15] | 林柏年.特种铸造[M].杭州:浙江大学出版社,2004 |
| [16] | 闫焉服,熊守美,柳百成,Mei Li,John Allison.铸造压力对ADC12Z压铸件孔洞和力学性能的影响[J].铸造,2007(11):1171-1174. |
| [17] | S.G. Lee;A.M. Gokhale;G.R. Patel;M. Evans .Effect of process parameters on porosity distributions in high-pressure die-cast AM50 Mg-alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1/2):99-111. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%