采用碳纳米管电泳沉积到碳纤维表面，达到改性碳纤维复合材料界面性能的目的．将羧基化的碳纳米管在十六烷基三甲基溴化铵的分散作用下制备成不同浓度的水溶液，在电场作用下，将碳纳米管电泳沉积到碳纤维表面．通过扫描电子显微镜、X－射线光电子能谱以及动态接触角对处理前后的碳纤维的表面形貌、表面元素及浸润性进行表征．研究结果表明，经过电泳沉积碳纳米管后，碳纤维的表面粗糙度、表面极性官能团含量及表面能都有较大提高，纤维的浸润性得到提高．对复合材料的界面性能分析表明，复合材料的界面性能在经过处理后有很大提高，当碳纳米管的质量浓度为0．1％，界面剪切强度提高了72．93％．
This article aims at improving interface performance of composite by electrophoretic depositing carbon nanotube on carbon fiber. Cetyl trimethyl ammonium bromide is used to fabricate the carboxyl carbon nanotubes solution with different concentration. Under the electric field, the carbon nanotube was deposited onto the surface of carbon fiber. By scanning electron microscopy ( SEM) , X?ray photoelectron spectroscopy ( XPS) and the Dynamic contact angle, the fiber surface morphology, surface elements and wettability were characterized. The results showed that, after electrophoretic deposition of carbon nanotubes, the surface roughness, number of polar groups and surface energy of carbon fiber increased significantly, which were the main reasons for improving the wettability between the carbon fiber and epoxy resin. The interfacial shear stress ( IFSS) increased to 72.93% when the concentration of carbon nanotubes was 0.1%.
参考文献
| [1] | 赵玉庭,姚西曾.复合材料基体与界面[M].上海:华东化工学院出版社,1991:186-193.,1991. |
| [2] | GAO Shanglin, MÄDER Edith, ZHANDAROV Serge F. Carbon fibers and composites with epoxy resin:topography, fractography and interphases[J]. Carbon, 2004, 42:515-529.,2004. |
| [3] | 赵稼祥.碳纤维的现状与新发展[J].材料工程,1997(12):3. |
| [4] | KINGSLEY K C H, ADAM F L, BISMARCK A. Fluorination of carbon fibres in atmospheric plasma [J]. Carbon, 2007, 45(4):775-784.,2007. |
| [5] | KINGSLEY K C H, LAMORINIERE S, KALINKA G, et al. Interfacial behavior between atmospheric-plasma-fluorinated carbon fibers and poly (vinylidene fluoride) [J]. Journal of Colloid and Interface Science, 2007, 313(2):476-484.,2007. |
| [6] | LU C, CHEN P, YU Q. Interfacial adhesion of plas-ma-treated carbon fiber/poly (phthalazinone ether sul-fone ketone) composite[J]. Journal of Applied Poly-mer Science, 2007, 106(3):1733-1741.,2007. |
| [7] | LI J, SUN F F. The interfacial feature of thermoplastic polystyrene composite filled with nitric acid oxidized carbon fiber [J]. Surface and Interface Analysis, 2009, 41(7):255-258.,2009. |
| [8] | MENG L H, CHEN Z W, SONG X L . Influence of high temperature and pressure ammonia solution treatment on interfacial behavior of carbon fiber/epoxy resin composites[J].Journal of Applied Polymer Science,2009,113(6):3436-3441.,2009. |
| [9] | FUKUNAGA A, UEDA S, NAGUMO M . Air-oxidation and anodization of pitch-based carbon fibers[J].Carbon,1999,37(7):1081-1085.,1999. |
| [10] | LI L. Interfacial studies on the ozone and air-oxidation-modified carbon fiber reinforced PEEK composites[J]. Surface and Interface Analysis, 2009, 41(4):310-315.,2009. |
| [11] | NAGANUMA T, NAITO K, YANG J M. The effect of a compliant polyimide nanocoating on the tensile properties of a high strength PAN-based carbon fiber [J]. Composites Science and Technology, 2009, 69 (7-8):1319-1322.,2009. |
| [12] | SAGER R J, KLEIN P J, LAGOUDAS D C. Effect of carbon nanotubes on the interfacial shear strength of T650 carbon fiber in an epoxy matrix[J]. Composites Science and Technology, 2009, 69(7-8):898-904.,2009. |
| [13] | JIANG Z X, LIU L, HUANG Y D. Influence of coupling agent chain lengths on interfacial performances of carbon fiber and polyarylacetylene resin composites[J]. Surface and Interface Analysis, 2009, 41(7):624-631.,2009. |
| [14] | 李宝峰,王浩静,朱星明,孟庆杰,于法涛,张淑彬.碳纤维表面嫁接马来酸对碳纤维复合材料力学性能的影响[J].化工新型材料,2008(10):81-83. |
| [15] | 刘丽,傅宏俊,黄玉东,杨明.碳纤维表面处理及其对碳纤维/聚芳基乙炔复合材料力学性能的影响[J].航空材料学报,2005(02):59-62. |
| [16] | LI K Z, WANG C, LI H J. Effect of chemical vapor deposition treatment of carbon fibers on the reflectivity of carbon fiber-reinforced cement-based composites [J]. Composites Science and Technology, 2008, 68 (5):1105-1114.,2008. |
| [17] | WANG C, LI K Z, LI H J. Influence of CVI treatment of carbon fibers on the electromagnetic interference of CFRC composites [J]. Cement and Concrete Composites, 2008, 30(6):478-485.,2008. |
| [18] | 邱桂花,夏和生,王琪.聚合物/碳纳米管复合材料研究进展[J].高分子材料科学与工程,2002(06):20-23,28. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%