采用切片法,对3mm厚2024铝合金和AZ31镁合金异种金属搅拌摩擦连接对接接头从截面和表面两个方向逐步层切,对每一截面抛光、腐蚀、拍照,并通过二维图像对接头进行了简单的三维重构,从而确定了3mm厚铝/镁合金异种搅拌摩擦连接接头的金属材料流动状况.结果表明,接头垂直方向不同层面的金属流动模式不同,同一层面前进侧和后退侧关于对接中心线材料流动也不对称.锯齿间距等于进给速度和搅拌头转速的比值表明,搅拌头每旋转一周,材料在搅拌头后部完成一次堆积.接头中下部的孔洞缺陷是由材料流动不充分造成的.低转速进给速度比的工艺参数使得材料流动主要发生在水平层面.
参考文献
[1] | P. L Threadgill;A. J. Leonard;H. R. Shercliff.Friction stir welding of aluminium alloys[J].International Materials Reviews,20092(2):49-93. |
[2] | 吴安如;夏长清;王少武;王银娜.搅拌摩擦焊接技术的研究现状及其展望[J].材料导报,2005(4):85-88. |
[3] | T. DebRoy;H. K. D. H. Bhadeshia.Friction stir welding of dissimilar alloys - a perspective[J].Science and Technology of Welding and Joining,20104(4):266-270. |
[4] | R. Nandan;T. DebRoy;H.K.D.H. Bhadeshia.Recent advances in friction-stir welding - Process, weldment structure and properties[J].Progress in materials science,20086(6):980-1023. |
[5] | C. Liu;D.I. Chen;S. Bhole.Polishing-assisted galvanic corrosion in the dissimilar friction stir welded joint of AZ31 magnesium alloy to 2024 aluminum alloy[J].Materials Characterization,20095(5):370-376. |
[6] | Ying Li;l.E.Murr;j.c.McClure.SOLID-STATE FLOW VISUALIZATION IN THE FRICTION-STIR WELDING OF 2024 AL TO 6061AL[J].Scripta materialia,19999(9):1041-1046. |
[7] | 任淑荣;马宗义;陈礼清.搅拌摩擦焊接及其加工研究现状与展望[J].材料导报,2007(1):86-92. |
[8] | A.P. Reynolds.Flow visualization and simulation in FSW[J].Scripta materialia,20085(5):338-342. |
[9] | Pooya POURAHMAD;Mehrdad ABBASI.Al 6013/Mg搅拌摩擦焊接的材料流动及相变[J].中国有色金属学报(英文版),2013(05):1253-1261. |
[10] | 邓永芳;左敦稳;宋波.搅拌摩擦焊接偏心挤压流动模型[J].焊接学报,2013(12):41-45. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%