M/A岛是X100管线钢典型组织,对钢的强韧性有着重要的影响.利用热模拟和显微分析技术研究了冷却速度、变形量和等温温度对X100管线钢中M/A岛的影响规律.结果表明:随着冷速增加,M/A岛体积分数和平均尺寸都减小,由在晶界处分布的较大块状向板条间隙弥散分布的细小片层状转变;随着变形量增加,M/A岛体积分数先增加,变形量为40％达到最大,变形量达到50％时,M/A岛体积分数降低;快冷后随着等温温度升高,M/A岛平均尺寸增大,等温温度为450℃时体积分数最大,温度继续升高体积分数减小.观察到M/A岛形貌多呈棱角状、链条状、片条状和针状,分布在晶界和基体内,岛内精细结构观察到微孪晶马氏体.
参考文献
| [1] | 黄开文.X80和X100钢级管线钢的合金化原理和生产要点[J].轧钢,2004(06):55-58. |
| [2] | Yong Zhong;Furen Xiao;Jingwu Zhang.In situ TEM study of the effect of M/A films at gram boundaries on crack propagation in an ultra-fine acicular ferrite pipeline steel[J].Acta materialia,20062(2):435-443. |
| [3] | K.V.Sudhakar;E.S.Dwarakadasa.A study on fatigue crack growth in dual phase martensitic steel in air environment[J].Bulletin of Materials Science,20003(3):193-199. |
| [4] | 赵明纯;单以银;肖福仁;李玉海;杨柯.管线钢中针状铁素体的形成及其强韧性的分析[J].材料科学与工艺,2001(4):356-358. |
| [5] | J. Speer;D. K. Matlock;B. C. De Cooman;J. G. Schroth.Carbon partitioning into austenite after martensite transformation[J].Acta materialia,20039(9):2611-2622. |
| [6] | 郑晓飞;康永林;孟德亮;安守勇;夏佃秀;张增军.铬对抗大变形管线钢组织和性能的影响[J].钢铁研究学报,2010(11):45-49. |
| [7] | 赵杰;徐海峰;时捷;李箭;蒲健;曹文全.细晶强化和位错强化对中锰马氏体钢的强化作用[J].钢铁,2012(8):57-61. |
| [8] | 牛辉;刘清友;杨忠文;毕宗岳;贾书君;陈长青.基于应变设计用厚规格X80管线钢组织与性能关系[J].钢铁,2013(8):55-60. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%