采用钴基钎料及镍基合金粉料，分别在1170℃保温10min、60min 和120min 的钎焊工艺下，对 K452镍基铸造高温合金进行真空钎焊实验，通过扫描电镜和能谱分析仪进行了接头显微组织观察与物相分析，并测试钎焊接头的高温力学性能。结果表明：在保温60min 的工艺规范下，界面实现较好的结合，钎缝内部孔洞缺陷较少，钎缝组织均匀，有利于钎焊接头性能的提高；在更长的保温时间120min 下，钎缝内部又有蚀孔缺陷形成，且较多的白色块状化合物在合金粉颗粒间聚集长大，但界面结合良好，钎焊接头性能较高，900℃抗拉强度达到400MPa，900℃／100MPa 持久寿命为141 h55min。
Vacuum brazing of K452 superalloy was performed with cobalt-base filler metal and nickel-base superalloy powder under bra-zing conditions of 1 170℃ /10min,1 170℃ /60min and 1 170℃ /120min respectively.The microstructure of brazed joints was analyzed by using SEM and EDS,and the high-temperature mechanical properties were also studied.The results show that the sound joints with fine microstructure and rare pores are achieved under 1 170℃ /60min brazing procedure,due to the good quality of interface.The joints braze under 1 170℃ /120min show the highest mechanical properties because of better interface quality,the average 900℃ tensile strength of 400MPa and 900℃ /100MPa stress-rupture life of 141 h /55min.But there morepoles are presented,and many white parti-cles of compound congregated and grow up between the nickel-base superalloy powder in the brazing seam.
参考文献
| [1] | X.Z. Qin;J.T. Guo;C. Yuan;J.S. Hou;H.Q. Ye .Precipitation and thermal instability of M_(23)C_6 carbide in cast Ni-base superalloy K452[J].Materials Letters,2008(2):258-261. |
| [2] | 秦学智,郭建亭,袁超,侯介山,周兰章,叶恒强.两种铸造镍基高温合金在长期时效期间的微观组织和力学性能演变[J].金属学报,2010(02):213-220. |
| [3] | 杨苹,夏成宝.氩弧焊修复尾喷管裂纹[J].机械制造,2003(06):57-57. |
| [4] | 刘军和,唐晓辉,王克亮.某型发动机高压涡轮工作叶片叶尖裂纹修复方法[J].航空发动机,2008(03):31-34,26. |
| [5] | JOHNSON R N.Electro-spark deposition:principles and applications[A].Orlando,2002:87-92. |
| [6] | Xie YJ;Wang MC .Microstructural morphology of electrospark deposition layer of a high gamma prime superalloy[J].Surface & Coatings Technology,2006(3/4):691-698. |
| [7] | 王茂才,吴维(山文).先进的燃气轮机叶片激光修复技术[J].燃气轮机技术,2001(04):53-56. |
| [8] | M. B. Henderson;D. Arrell;R. Larsson .Nickel based superalloy welding practices for industrial gas turbine applications[J].Science and Technology of Welding and Joining,2004(1):13-21. |
| [9] | Kim DY.;Kim KS.;Youn JG.;Hwang JH. .A study on fusion repair process for a precipitation hardened IN738Ni-based superalloy[J].Journal of engineering for gas turbines and power: Transactions of the ASME,2000(3):457-461. |
| [10] | C.Y Su;W.C. Lih;C.P. Chou .Activated diffusion brazed repair for IN738 hot section components of gas turbines[J].Journal of Materials Processing Technology,2001(3):326-332. |
| [11] | LI X H;MAO W;CHENG Y Y et al.Microstruetures and properties of transient liquid phase diffusion bonded joints of DZ22 superalloy[J].Welding in the world,2005,49(1/2):34-38. |
| [12] | 李晓红,钟群鹏,曹春晓.DD3单晶合金瞬间过渡液相扩散焊接头组织与性能[J].航空材料学报,2003(02):1-5,24. |
| [13] | 李晓红,钟群鹏,曹春晓.K403与DZ4高温合金的大间隙钎焊[J].航空材料学报,2003(04):10-15. |
| [14] | 赵海生,潘晖,孙计生,李大斌.合金粉对K640钎缝组织及性能的影响[J].电焊机,2008(09):46-49. |
| [15] | 赵海生,潘晖,孙计生,李大斌.K640合金钎焊接头组织及工艺控制[J].材料工程,2008(09):17-19,24. |
| [16] | Xiao Huang;Warren Miglietti .Wide Gap Braze Repair of Gas Turbine Blades and Vanes - A Review[J].Journal of engineering for gas turbines and power: Transactions of the ASME,2012(1):010801-1-010801-17. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%