采用差示扫描量热法(DSC)和傅里叶变换红外光谱法(FTIR)研究一种碳纤维/环氧预浸料在微波辐射下的固化特性,并对碳纤维/环氧预浸料层合板的微波固化-真空袋成型工艺中存在的真空袋易过热破损的问题进行研究.结果表明:与热固化相比,微波固化能够明显缩短固化时间,而且不会改变最终固化产物的分子结构;碳纤维/环氧预浸料的尺寸大小对其微波固化行为有一定的影响;通过控制微波功率,可以有效地解决在碳纤维/环氧复合材料微波固化过程中存在的真空袋过热破损的问题,且微波固化可获得固化时间控制在60min左右、固化度达95%以上的碳纤维/环氧复合材料层合板,微波固化时间比传统热固化(固化时间大于2h)缩短了一半以上.
The curing behavior of a carbon fiber/epoxy prepreg under microwave radiation was investi-gated using differential scanning calorimetry (DSC)and Fourier transform infrared spectroscopy (FT-IR),respectively.The carbon fiber/epoxy composite laminates were manufactured through micro-wave curing-vacuum bag molding process,and the existing overheating and broken issues of vacuum bags were studied.The results show that compared with thermal curing,microwave curing can signif-icantly shorten curing time without altering molecular structure of the cured products.It seems that the size of the carbon fiber/epoxy prepreg influences its microwave curing characteristic.The problem of vacuum bag breakage,due to overheating in microwave curing of carbon fiber/epoxy composites, can be solved by controlling the microwave power,and the fabrication of the laminates with micro-wave radiation can be accomplished in about 60 minutes with more than 95% curing degree,indicating that microwave processing is shortened by more than half of curing time than conventional thermal cu-ring (curing time more than 2h).
参考文献
| [1] | 杜善义.先进复合材料与航空航天[J].复合材料学报,2007(01):1-12. |
| [2] | 陈祥宝.先进树脂基复合材料的发展和应用[J].航空材料学报,2003(z1):198-204. |
| [3] | 沈军;谢怀勤.先进复合材料在航空航天领域的研发与应用[J].材料科学与工艺,2008(5):737-740. |
| [4] | 益小苏;张明;安学锋;刘立朋.先进航空树脂基复合材料研究与应用进展[J].工程塑料应用,2009(10):72-76. |
| [5] | 杜善义;关志东.我国大型客机先进复合材料技术应对策略思考[J].复合材料学报,2008(1):1-10. |
| [6] | 初琳;赵晓莉;王丽娟.树脂基复合材料固化技术发展现状[J].化工装备技术,2013(1):43-46. |
| [7] | E. T. Thostenson;T. -W. Chou.Microwave processing: fundamentals and applications[J].Composites, Part A. Applied science and manufacturing,19999(9):1055-1071. |
| [8] | Jian Zhou;Chun Shi;Bingchu Mei;Runzhang Yuan;Zhengyi Fu.Research on the technology and the mechanical properties of the microwave processing of polymer[J].Journal of Materials Processing Technology,20031/3(1/3):156-158. |
| [9] | 陈名华;姚武文;王新坤;陈义参;葛文军.微波固化碳纤维/环氧树脂胶的研究[J].粘接,2005(6):13-15. |
| [10] | D.A. Papargyris;R.J. Day;A. Nesbitt;D. Bakavos.Comparison of the mechanical and physical properties of a carbon fibre epoxy composite manufactured by resin transfer moulding using conventional and microwave heating[J].Composites science and technology,20087/8(7/8):1854-1861. |
| [11] | 朱乃姝;马世宁;孙晓峰;樊雪峰.固化方式和纤维表面处理对碳纤维-树脂界面化学组成的影响[J].中国工程机械学报,2010(1):111-114. |
| [12] | 孙晓峰;马世宁;朱乃姝;钱海峰;胡春华.微波固化改性环氧树脂/碳纤维复合材料研究[J].材料工程,2008(z1):190-193,198. |
| [13] | C. Nightingale;R. J. Day.Flexural and interlaminar shear strength properties of carbon fibre/epoxy composites cured thermally and with microwave radiation[J].Composites, Part A. Applied science and manufacturing,20027(7):1021-1030. |
| [14] | Nanya Li;Yingguang Li;Xiang Hang;James Gao.Analysis and optimization of temperature distribution in carbon fiber reinforced composite materials during microwave curing process[J].Journal of Materials Processing Technology,20143(3):544-550. |
| [15] | Yumin Liu;Y.Xiao;X.Sun;D.A.Scola.Microwave Irradiation of Nadic-End-Capped Polyimide Resin (RP-46) and Glass-Graphite-RP-46 Composites: Cure and Process Studies[J].Journal of Applied Polymer Science,199912(12):2391-2411. |
| [16] | Garea SA;Iovu H.Microwave assisted crosslinking process of epoxy resins[J].Molecular Crystals and Liquid Crystals Science and Technology.Section A.Molecular Crystals and Liquid Crystals,20040(0):61-73. |
| [17] | Robert A. Witik;Fabrice Gaille;Remy Teuscher;Heike Ringwald;Veronique Michaud;Jan-Anders E. Manson.Economic and environmental assessment of alternative production methods for composite aircraft components[J].Journal of cleaner production,2012:91-102. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%