研究热压成型过程中，不同固化温度对亚麻纤维及其增强复合材料力学性能的影响。结果表明：亚麻纤维在120，140℃和180℃分别处理2h 后单纤维拉伸性能发生不同程度的下降。环氧树脂 E-51在120，140℃和180℃下固化2h 后拉伸性能未发生明显变化。基于环氧树脂的单向亚麻纱线增强复合材料分别在120℃和140℃固化成型时，拉伸强度和冲击强度变化不大。但当固化温度达到180℃时，由于亚麻纤维在高温环境下损伤较为严重，其增强复合材料的拉伸强度和冲击强度均发生明显的下降。然而复合材料的拉伸模量随着成型温度的升高有一定幅度的提升。
The effect of different curing temperatures on the mechanical properties of flax fiber and their reinforced composites was studied during hot pressing forming process.The results show that the tensile strength of single flax fiber declines in varying degrees when flax fibers are treated for 2h at 120,140℃ and 180℃,respectively,the tensile strength of epoxy resin E-51 has a little change after treated at the same conditions.Tensile and impact strength change slightly,when unidirectional flax yarn reinforced epoxy resin composites is cured under 120℃ and 140℃.However,when the curing temperature increases to 180℃,owing to the serious damage of flax fiber at high temperature,the tensile and impact strength of the flax fiber reinforced composites then decrease obviously.Mean-while,as the curing temperature increases,the tensile modulus of composites improves in some degree.
参考文献
| [1] | Li Y.;Mai Y.W. .Sisal fibre and its composites: a review of recent developments[J].Composites science and technology,2000(11):2037-2055. |
| [2] | 刘燕峰,包建文,李艳亮,益小苏.单向苎麻纤维增强酚醛树脂复合材料性能的研究[J].航空材料学报,2011(06):68-72. |
| [3] | 陈旭,尹鹏,咸贵军,刘燕峰,刘青曼,益小苏.苎麻纤维增强酚醛树脂基复合材料的湿热性能研究[J].航空材料学报,2013(02):58-65. |
| [4] | 李岩,罗业.天然纤维增强复合材料力学性能及其应用[J].固体力学学报,2010(06):613-630. |
| [5] | SILVA F A;CHAWLA N;FILHO R D T .Tensile behaviour of high performance natural (sisal)fibers[J].Composites Science and Technology,2008,68(15-16):3438-3443. |
| [6] | 田永,何莉萍,王璐琳,屈伟平.汽车制造用苎麻纤维增强聚丙烯的力学性能研究[J].材料工程,2008(01):21-24,33. |
| [7] | Y. Li;Y. Luo;S. Han .Multi-Scale Structures of Natural Fibres and Their Applications in Making Automobile Parts[J].Journal of Biobased Materials and Bioenergy,2010(2):164-171. |
| [8] | BALEY C .Analysis of the flax fibres tensile behaviour and analy-sis of the tensile stiffness increase[J].Composites Part A:Ap-plied Science and Manufacturing,2002,33(07):939-948. |
| [9] | YANG WeiDong,LI Yan.Sound absorption performance of natural fibers and their composites[J].中国科学:技术科学（英文版）,2012(08):2278-2283. |
| [10] | ZHENG Z Y;LI Y;YANG W D .Absorption properties of nat-ural fiber-reinforced sandwich structures based on the fabric structures[J].Journal of Reinforced Plastics and Composites,2013,32(20):1561-1568. |
| [11] | LIU K;TAKAGI H;OSUGI R et al.Effect of lumen size on the effective transverse thermal conductivity of unidirectional natural fiber composites[J].Composites Science and Technolo-gy,2012,72(05):633-639. |
| [12] | 刘燕峰,包建文,李艳亮,益小苏.固化温度对苎麻纤维增强复合材料性能的影响[J].航空材料学报,2012(02):49-53. |
| [13] | BISANDA E T N;ANSELL M P .Properties of sisal-CNSL composites[J].Journal of Materials Science,1992,27(06):1690-1700. |
| [14] | SRIDHAR M K;BASAVARAJJAPPA G;KASTURI S S.Thermal stability of jute fibres[J].Indian Journal of Fibre and Textile Research,1982(07):87-91. |
| [15] | GONZALEZ C;MEYERS G E .Thermal-degradation of wood fillers at the melt-processing temperatures of wood-plastic com-posites:Effects on wood mechanical-properties and production of volatiles[J].International Journal of Polymeric Materials and Polymeric Biomaterials,1993,23(1 -2):67-85. |
| [16] | MUNAWAR S S;UNEMURA K;KAWAI S .Characterization of the morphological,physical,and mechanical properties of seven nonwood plant fiber bundles[J].Journal of Wood Sci-ence,2007,53(02):108-113. |
| [17] | CHAND N;HASHMI S A R .Mechanical properties of sisal fi-bre at elevated temperatures[J].Journal of Materials Science,1993,28(24):6724-6728. |
| [18] | VAN D E VELDE K;KIEKENS P .Thermoplastic pultrusion of natural fiber reinforced composites[J].Computers & Structures,2001,54(2-3):355-360. |
| [19] | 李贤军;刘元;高建民 等.高温热处理木材的 FTIR 和 XRD 分析[J].北京林业大学学报,2009,31(增刊 1):104-107. |
| [20] | 龙超,郝丙业,刘文斌,雷得定.影响热处理木材力学性能的主要工艺因素[J].木材工业,2008(01):43-45. |
| [21] | SHAH D;SCHUBEL PJ;CLIFFORD M J et al.The tensile behavior of off-axis loaded plant fiber composites:an insight on the non-linear stress-strain response[J].Polymer Composites,2012,33(09):1494-1504. |
| [22] | MA H;LI Y;WANG D .Investigations of fiber twist on the mechanical properties of sisal fiber yarns and their composites[J].Journal of Reinforced Plastics and Composites,2014,33(07):687-696. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%