利用高温熔体反应法成功制备Al-5Ti-1B细化剂.通过热力学计算,确定Al-5Ti-1B细化剂的起始反应温度,研究熔体温度对细化剂组织形貌及吸收率的影响.利用X射线衍射,扫描电子显微镜和X射线能谱仪观察细化剂的相组成和形貌,同时对Al-5Ti-1B细化剂铸锭进行高温挤压,并对挤压出的φ9.5mm丝材进行微观组织分析和细化实验.结果表明:细化剂主要由TiB2,TiAl3,α-Al相组成;850℃制备的细化剂铸锭组织形貌最佳,且Ti和B吸收率达到最佳匹配.挤压后TiAl3相呈细小的块状和TiB2弥散分布在基体内.添加0.2%(质量分数)细化剂后,纯铝的晶粒尺寸由3.99mm细化到0.45mm.
Al-5Ti-1B refiner was successfully prepared by melt reaction method .Through the thermo-dynamics calculation ,the initial reaction temperature was determined .The influence of reaction tem-perature on microstructure and absorption rate of the alloy was investigated .The phase and micro-structure of the alloy were observed by X-ray diffraction ,scanning electron microscope and energy dis-persive spectrometer .The Al-5Ti-1B refiner was extruded at high temperature to wire with the diame-ter of 9 .5mm ,and then the refinement experiment was carried out on pure aluminium .The results in-dicate that the refiner consists of TiB2 ,TiAl3 and α-Al ,and the microstructure prepared at 850℃ is the optimum and the absorption rate of Ti and B matches the best .The TiAl3 and TiB2 phases distrib-ute homogeneously in the matrix after extrusion .When adding 0 .2% (mass fraction) of Al-5Ti-1B re-finer ,the grain size of pure aluminium reduces from 3 .99mm to 0 .45mm .
参考文献
| [1] | Yucel Birol.Al-Ti-B grain refiners via powder metallurgy processing of Al/K_2TiF_6/KBF_4 powder blends[J].Journal of Alloys and Compounds,20092(2):311-314. |
| [2] | 黄元春;杜志勇;肖政兵;颜徐宇.Al-Ti-C 和 Al-Ti-B 对7050铝合金微观组织与力学性能的影响[J].材料工程,2015(12):75-80. |
| [3] | 高耸;疏达;王镭;韩延峰;王俊;孙宝德.Al-Ti-B晶粒细化剂的研究进展[J].轻合金加工技术,2007(12):7-10,50. |
| [4] | Pourkia, N.;Emamy, M.;Farhangi, H.;Ebrahimi, S.H.S..The effect of Ti and Zr elements and cooling rate on the microstructure and tensile properties of a new developed super high-strength aluminum alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,201020(20):5318-5325. |
| [5] | B. S. Murty;S. A. Kori;M. Chakraborty.Grain refinement of aluminium and its alloys by heterogeneous nucleation and alloying[J].International Materials Reviews,20021(1):3-29. |
| [6] | 贺永东;张新明;曹志强.微量Cr、Mn、Zr、Ti、B元素对铸态AlZnMgCu合金的晶粒细化效果的影响[J].稀有金属材料与工程,2010(7):1135-1140. |
| [7] | Enzhao Wang;Tong Gao;Jinfeng Nie.Grain refinement limit and mechanical properties of 6063 alloy inoculated by Al-Ti-C (B) master alloys[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2014:7-11. |
| [8] | MA Tengfei;CHEN Ziyong;NIE Zuoren;HUANG Hui.Microstructure of Al-Ti-B-Er refiner and its grain refining performance[J].稀土学报（英文版）,2013(06):622-627. |
| [9] | 曹富荣;温景林;丁桦;王昭东;李英龙;管仁国;侯辉.带扩展腔的纯铝及铝钛硼合金连续挤压力的分析与实验研究[J].中国有色金属学报（英文版）,2013(1):201-207. |
| [10] | E. G. Kandalova;V. I. Nikitin;Jie Wanqi.Effect of Al powder content on SHS Al-Ti grain refiner[J].Materials Letters,20022/3(2/3):131-134. |
| [11] | YiicelBirol.Production of Al-Ti-B grain refining master alloys from Na_2B_4O_7 and K_2 TiF_6[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,20081/2(1/2):271-276. |
| [12] | Nikitin V.I.;Wnqi J.I.E..Preparation of Al-Ti-B grain refiner by SHS technology[J].Scripta materialia,20006(6):561-566. |
| [13] | 王衍行;林均品;贺跃辉;王艳丽;陈国良.元素粉末Ti与Al反应机理的研究进展[J].材料导报,2007(1):83-85. |
| [14] | YE Yi-cong;HE Liang-ju;LI Pei-jie.Differences of grain-refining effect of Sc and Ti additions in aluminum by empirical electron theory analysis[J].中国有色金属学报（英文版）,2010(03):465-470. |
| [15] | Peijie Li;E.G. Kandalova;V.I. Nikitin.Grain refining performance of Al-Ti master alloys with different microstructures[J].Materials Letters,20056(6):723-727. |
| [16] | Peijie Li;E.G. Kandalova;V.I. Nikitin;A.R. Luts;A.G. Makarenko;Yanfei Zhang.Effect of fluxes on structure formation of SHS Al―Ti―B grain refiner[J].Materials Letters,200322/23(22/23):3694-3698. |
| [17] | Yucel Birol.The effect of holding conditions in the conventional halide salt process on the performance of Al-Ti-B grain refiner alloys[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,20071/2(1/2):142-147. |
| [18] | Yucel Birol.Production of Al-Ti-B master alloys from Ti sponge and KBF_4[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,20071/2(1/2):108-112. |
| [19] | V. Auradi;S.A. Kori.Influence of reaction temperature for the manufacturing of Al-3Ti and Al-3B master alloys[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,20081/2(1/2):147-156. |
| [20] | M.-X. Zhang;P. M. Kelly;M. A. Easton.Crystallographic study of grain refinement in aluminum alloys using the edge-to-edge matching model[J].Acta materialia,20055(5):1427-1438. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%