以稻壳、Al2O3和M9O为主要原料,按偏镁铝方案确定堇青石的组成,并以堇青石与莫来石质量比为7∶3进行配料,再掺少量Nd2O3为烧结助剂,用一步法烧成了堇青石-莫来石多孔陶瓷.测定了烧结试样的抗弯强度、显气孔率、热膨胀系数,用XRD分析了试样在烧结过程中的物相组成变化,并用SEM观察其显微结构.研究结果表明:在掺2％Nd2O3,1380℃保温5h条件下,制备的多孔陶瓷的抗弯强度为20.55MPa,显气孔率48.34％,热膨胀系数3.5×10-6·℃-1,其主晶相为堇青石和莫来石,SEM显示晶体间存在大量孔隙.
参考文献
| [1] | 李小龙;周健儿;肖卓豪;包启富.高温含尘废气净化用堇青石质多孔陶瓷过滤膜层的制备研究[J].陶瓷学报,2013(4):402-408. |
| [2] | Al-Harbi, Omar A.;Ozgur, Cem;Khan, M. M..Fabrication and characterization of single phase cordierite honeycomb monolith with porous wall from natural raw materials as catalyst support[J].CERAMICS INTERNATIONAL,20153 Pt.A(3 Pt.A):3526-3532. |
| [3] | Shaohong Wang;Haoran Lu;Zhaoxia Hou.Sol-emulsion-gel synthesis of cordierite ceramics for high-frequency multilayer chip inductors[J].CERAMICS INTERNATIONAL,20132(2):991-997. |
| [4] | Ye Li;Haoran Qian;Xudong Cheng;Ruifang Zhang;Heping Zhang.Fabrication of dense cordierite ceramic through reducing Al_2O_3 mole ratio[J].Materials Letters,2014Feb.1(Feb.1):262-264. |
| [5] | 张巍.堇青石综合利用现状与展望[J].矿物岩石地球化学通报,2015(02):426-442. |
| [6] | 刘建东;黄张根;李哲;郭倩倩;李巧艳.Ce对Mn/TiO2/堇青石整体低温脱硝选择性催化还原催化剂的改性[J].高等学校化学学报,2014(3):589-595. |
| [7] | 徐晓虹;马雄华;吴建锋;张亚祥;劳新斌;张锋意.太阳能热发电用堇青石-莫来石复相陶瓷的制备及抗热震性[J].武汉理工大学学报,2012(1):1-6. |
| [8] | 微波冶金用堇青石莫来石耐火材料制备及性能[J].材料科学与工艺,2011(3):32-36. |
| [9] | W. Yan;N. Li;J. Tong.Effect of Particle Size on the Pore Characterization and Strength of Porous Cordierite-mullite Ceramics Prepared by a Pore- forming in-situ Technique[J].Science of sintering,20132(2):165-172. |
| [10] | XU Xiaohong;MA Xionghua;WU Jianfeng;CHEN Ling;XU Tao;ZHANG Mengqi.In-Situ Preparation and Thermal Shock Resistance of Mullite-Cordierite Heat Tube Material for Solar Thermal Power[J].武汉理工大学学报（材料科学版）（英文版）,2013(3):407-412. |
| [11] | 温海琴;席红安;李勤;张继周;陈雷;王若钉.原位反应烧成莫来石-堇青石复合材料及其特性[J].硅酸盐学报,2010(2):347-351. |
| [12] | 杨现锋;李勇;徐协文;蔡星;谢志鹏.凝胶注模堇青石-莫来石复相材料的制备及其抗热震性能[J].硅酸盐学报,2014(9):1179-1183. |
| [13] | 方斌祥;朱伯铨;王志强.高强度堇青石-莫来石棚板的研制[J].耐火材料,2009(1):51-53. |
| [14] | 白建光;赵敬忠.莫来石含量对堇青石-莫来石复相陶瓷性能的影响[J].耐火材料,2008(5):365-367. |
| [15] | 罗旭东;曲殿利;谢志鹏.La3+,Ce4+对制备堇青石材料晶相转变及烧结性能的影响[J].中国稀土学报,2013(2):203-210. |
| [16] | 李国华;陈树江;田琳;郝明选;袁林.氧化镧对水泥窑用方镁石-复合尖晶石砖结构与性能的影响[J].中国稀土学报,2015(1):106-110. |
| [17] | 史志铭;梁开明;顾守仁.液相烧结中液相成份对堇青石相变和陶瓷显微组织的影响[J].清华大学学报(自然科学版),2001(10):27-29. |
| [18] | 唐志阳.稀土氧化物在陶瓷中的应用[J].山东陶瓷,2005(02):16-19. |
| [19] | 郭伟;陆洪彬;冯春霞;余海涛.Nd2O3对稻壳合成多孔堇青石陶瓷的影响[J].人工晶体学报,2010(4):1025-1029. |
| [20] | 田忠凯;王周福;王玺堂;张保国.Nd2O3对反应烧结合成镁铝尖晶石的影响[J].武汉科技大学学报（自然科学版）,2008(4):377-380. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%